手表装饰用类金刚石薄膜的性能研究

发布时间：2018-05-16 00:32

  本文选题：不锈钢 + 类金刚石薄膜　； 参考：《电镀与涂饰》2017年08期

【摘要】：采用多弧离子镀与离子束辅助磁控溅射复合工艺在316L不锈钢上制备了手表装饰用类金刚石(DLC)梯度薄膜(Cr WC DLC),研究了薄膜的外观、组成、硬度、耐蚀性、耐磨性、防刮花性能及结合力。结果表明,该方法制得的DLC梯度薄膜呈亮黑色且均匀一致,硬度达28GPa,sp~3结构含量约53%,具有优良的结合强度和耐蚀、耐磨、防刮花性能,是理想的手表用装饰性膜层。
[Abstract]:Diamond like carbon (DLC) gradient film for watch decoration was prepared on 316L stainless steel by multi-arc ion plating and ion beam assisted magnetron sputtering. The appearance, composition, hardness, corrosion resistance and wear resistance of the films were studied. Anti-scraping performance and adhesion. The results show that the DLC gradient films prepared by this method are bright black and uniform. The hardness of the films is about 53%, which has excellent bonding strength, corrosion resistance, wear-resistance and anti-scratch performance. It is an ideal decorative coating for watches.
【作者单位】： 华南理工大学材料科学与工程学院;珠海罗西尼表业有限公司;
【分类号】：TG174.4

【相似文献】

相关期刊论文 前10条

1 胡芳;代明江;林松盛;罗顺;侯惠君;石倩;韦春贝;;含氢掺硅类金刚石薄膜的制备及性能表征[J];中国表面工程;2012年06期

2 欧玉静;王永富;张俊彦;;水分子诱导类金刚石薄膜表面的变化[J];中国表面工程;2013年06期

3 江河清,黄丽娜,张治军,徐洮,刘维民;液相电沉积类金刚石薄膜的组成及结构分析[J];功能材料;2004年05期

4 苗树翻;严一心;杭凌侠;;不锈钢(3Cr13)镀类金刚石薄膜的研究[J];西安工业大学学报;2006年02期

5 江河清,张治军,徐洮,刘维民;液相电沉积类金刚石薄膜的研究进展[J];表面技术;2004年02期

6 吴玲玲,梁海峰,蔡长龙,徐均琪,杭凌侠,严一心;钛镍合金上制备类金刚石薄膜的性能研究[J];表面技术;2005年02期

7 尹路;陈洁;;氮对纯钛表面类金刚石薄膜内应力与附着力的影响(英文)[J];稀有金属材料与工程;2012年S2期

8 周顺,严一心;脉冲真空电弧离子镀在不锈钢上沉积类金刚石薄膜的研究[J];真空;2005年04期

9 郭力军，许念坎，刘正堂，，张贵锋，郑修麟;极板负偏压对类金刚石薄膜性质的影响[J];材料研究学报;1994年01期

10 杜景永;张贵锋;李国卿;侯晓多;;不锈钢上液相电沉积类金刚石薄膜[J];电化学;2007年01期

相关会议论文 前3条

1 王娟;张溪文;韩高荣;;铝基表面等离子增强化学气相法沉积类金刚石薄膜研究[A];第六届华东三省一市真空学术交流会论文集[C];2009年

2 胡芳;代明江;林松盛;;微喷砂预处理对硬质合金上沉积类金刚石薄膜结合力的影响[A];TFC’09全国薄膜技术学术研讨会论文摘要集[C];2009年

3 冷永祥;孙鸿;黄楠;;工程材料表面改性-类金刚石薄膜及氮化钛薄膜研究及应用[A];中国真空学会2006年学术会议论文摘要集[C];2006年

相关博士学位论文 前1条

1 代明江;类金刚石薄膜掺杂作用机理及其摩擦学性能[D];华南理工大学;2016年

相关硕士学位论文 前1条

1 吴楠;AZ31镁合金及其表面沉积类金刚石薄膜腐蚀行为的研究[D];辽宁科技大学;2014年

本文编号：1894649