建筑装饰用Cu-Ni合金的腐蚀行为研究

发布时间：2019-01-04 19:20

【摘要】：通过浸泡静态腐蚀和电化学试验方法,研究了不同浸泡时间下建筑装饰用Cu-Ni合金的腐蚀行为。结果表明,随着浸泡时间的延长,铜合金的腐蚀速率逐渐降低;铜合金的表面腐蚀膜层的颜色逐渐从紫红色、棕色、黄绿色转变为墨绿色;腐蚀初期的产物主要为Cu_2O,随着腐蚀时间延长过渡为Cu_2O和CuO;继续延长腐蚀时间,腐蚀产物膜层不断增厚,外层腐蚀产物膜中的Cu_2O与溶液中的Cl-发生反应生成Cu_2(OH)_3Cl;致密均匀的腐蚀产物膜层在一定程度上抑制了腐蚀反应的进行,使得腐蚀速率逐渐降低。
[Abstract]:The corrosion behavior of Cu-Ni alloy for architectural decoration under different immersion time was studied by immersion static corrosion and electrochemical test. The results show that the corrosion rate of copper alloy decreases with the prolongation of soaking time, and the color of corrosion film on the surface of copper alloy changes from purplish red, brown and yellowish green to dark green. The main products at the beginning of corrosion are Cu_2O, which transition to Cu_2O and CuO; with the prolongation of corrosion time. As the corrosion time continues to be prolonged, the corrosion product film becomes thicker, and the Cu_2O in the outer layer of the corrosion product film reacts with the Cl- in the solution to form Cu_2 (OH) _ 3Cl. The dense and uniform corrosion product film inhibited the corrosion reaction to a certain extent and gradually reduced the corrosion rate.
【作者单位】： 广西科技大学鹿山学院;广西铜业有限公司;
【分类号】：TG178

【相似文献】

相关期刊论文 前5条

1 L.J.P.德罗莱恩加;杜桂枝;;合金成分及显微组织对Cu-Ni合金在海水中的腐蚀性状的影响[J];国外舰船技术(材料类);1984年08期

2 谢发勤,李金山,傅恒志;Cu-Ni单相合金的深过冷定向凝固过程研究[J];科学通报;1999年18期

3 季杰,张文钺,刘力,张树生;新型Cu-Ni合金PTA堆焊材料及其耐蚀性[J];焊接学报;2000年02期

4 易勇;丁志杰;蒋代忠;李恺;;非晶态Cu-Ni合金的分子动力学模拟[J];山西大学学报(自然科学版);2010年04期

5 杨春,魏炳波,陈民,过增元;液态Cu-Ni合金的超过冷与热力学性质[J];清华大学学报(自然科学版);2001年08期

相关会议论文 前3条

1 曹中秋;牛焱;吴维;;中间Ni含量的Cu-Ni合金在800℃空气中的氧化[A];2000年材料科学与工程新进展（下）——2000年中国材料研讨会论文集[C];2000年

2 季杰;李彤;;Cu-Ni合金堆焊层的腐蚀行为[A];全面建设小康社会：中国科技工作者的历史责任——中国科协2003年学术年会论文集（上）[C];2003年

3 郭学锋;杨根仓;邢建东;;过冷Cu-Ni熔体在惰性形核涂层铸型中过冷遗传性[A];面向21世纪的科技进步与社会经济发展（下册）[C];1999年

相关硕士学位论文 前2条

1 徐磊;Cu-Ni基合金导杆材料的成分设计及其抗氧化和耐腐蚀性能研究[D];中南大学;2009年

2 熊慧文;Cu-Ni/（10NiO-NiFe_2O_4）金属陶瓷的氧化与熔盐腐蚀行为的研究[D];中南大学;2012年

，

本文编号：2400689