【摘要】：以分子量为2000的聚己内酯(PCL)作为软段,六亚甲基二异氰酸酯(HMDI)作为硬段,分子量为250的聚四氢呋喃(PTMG)为扩链剂,通过调整不同软硬段的比例,合成了5组具有不同特性的可降解聚氨酯材料,并对相应的聚氨酯的分子量、力学性能、热性能等进行了研究,同时以不同特性的PU为基础,构建出了具有多力学层区结构的多孔软骨组织工程支架,并对其孔隙结构进行了分析。
[Abstract]:The polycaprolactone (PCL) with molecular weight of 2000 was used as soft segment, hexamethylene diisocyanate (HMDI) as hard segment and polytetrahydrofuran (PTMGG) with molecular weight 250 as chain extender. By adjusting the ratio of different soft and hard segments, Five groups of degradable polyurethane materials with different properties were synthesized, and their molecular weight, mechanical properties and thermal properties were studied. The porous cartilage tissue engineering scaffold with multi-layer structure was constructed and its pore structure was analyzed.
【作者单位】： 华南理工大学;国家人体组织功能重建工程技术研究中心;
【基金】：教育部新世纪优秀人才支持计划项目(NCET-12-0200) 广州市科技计划项目(2012J4100124)
【分类号】：O631.3;R318.08

【共引文献】

相关期刊论文 前10条

1 Ni-jia Song;Xia Jiang;Jie-hua Li;Yong Pang;Jian-shu Li;Hong Tan;Qiang Fu;;THE DEGRADATION AND BIOCOMPATIBILITY OF WATERBORNE BIODEGRADABLE POLYURETHANES FOR TISSUE ENGINEERING[J];Chinese Journal of Polymer Science;2013年10期

2 王芋骁;孔志杰;黄溪;马林;;交联改性丝素蛋白材料制备和医学应用[J];现代丝绸科学与技术;2013年05期

3 郭立强;;聚乳酸-羟基乙酸共聚物的研究进展[J];化工技术与开发;2014年05期

4 黎庆安;范昌平;;水性聚氨酯层压胶的制备及性能[J];广东化工;2014年15期

5 李新s，

本文编号：1573564