基于多巴胺的铁表面改性和血液相容性评价

发布时间：2018-03-18 05:11

  本文选题：铁　切入点：多巴胺　出处：《稀有金属材料与工程》2014年S1期 　论文类型：期刊论文

【摘要】：为了提高可降解材料铁的血液相容性,利用盐酸多巴胺在碱性条件下能发生自发聚合的特性,对铁表面进行了改性研究。由于聚多巴胺表面有活性反应基团,从而可以将BSA(牛血清白蛋白)固载到铁表面。利用FESEM、AFM、FTIR-ATR、接触角测定、MTT实验、溶血和血小板实验等对铁表面膜层的形貌、成分、亲水性、细胞毒性和血液相容性进行了研究。结果表明,在铁表面成功地修饰上了聚多巴胺BSA膜层,并且膜层没有明显的细胞毒性,能有效减少血小板的粘附。
[Abstract]:In order to improve the blood compatibility of degradable iron, the surface of iron was modified by the spontaneous polymerization of dopamine hydrochloride under alkaline conditions. In this way, BSA (bovine serum albumin) was immobilized on the surface of iron. The morphology, composition and hydrophilicity of the film on iron surface were determined by contact angle, MTT test, hemolysis and platelet test, using Fesemer AFMU FTIR-ATR. Cytotoxicity and blood compatibility were studied. The results showed that the polydopamine BSA film was successfully modified on the iron surface, and the membrane had no obvious cytotoxicity, which could effectively reduce the adhesion of platelets.
【作者单位】： 北京大学;
【基金】：国家自然科学基金(31070846,30870623)
【分类号】：R318.08

【相似文献】

相关期刊论文 前10条

1 潘长江,王进,黄楠,孙鸿,杨苹,冷永祥,陈俊英,万国江;等离子体表面接枝改性聚对苯二甲酸乙二醇酯的血液相容性研究[J];功能材料;2003年04期

2 吴玉厚,张善锋,刘殿红,李言秋,周国利;血液相容性材料研究进展[J];聊城大学学报(自然科学版);2003年02期

3 谭鸿,李洁华,谢兴益,郭敏,傅强,钟银屏;含氟聚醚聚氨酯与聚醚聚氨酯共混的表面结构及血液相容性的研究[J];生物医学工程学杂志;2004年04期

4 魏文,程为庄;血液相容性及表面改性的研究[J];高分子通报;2004年05期

5 王琴梅,滕伟,潘仕荣,张静夏;聚谷氨酸苄酯/聚乙二醇嵌段共聚物膜的血液相容性研究[J];生物医学工程学杂志;2005年01期

6 浦鸣;计剑;李晓林;沈家骢;;水溶性梳状聚乙二醇构建的血液相容性涂层[J];高分子学报;2006年05期

7 欧阳晨曦;李沁;王维慈;周飞;徐卫林;李文斌;;小口径人工血管血液相容性[J];中国组织工程研究与临床康复;2008年06期

8 梅恒;胡豫;张治华;王华芳;郭涛;魏文宁;;二氧化钛纳米材料对家兔血液相容性影响[J];中国公共卫生;2010年01期

9 习羽;贺春丽;杨桑;朱皓淼;黄小波;李利;周宁琳;章峻;沈健;;聚乙烯表面亲水化改性及其血液相容性改进[J];功能材料;2011年08期

10 伏鹏;刘成s，

本文编号：1628133