Abundant photoelectronic behaviors of La 0.67 Sr 0.33 MnO 3

发布时间：2021-10-25 03:12

　　Temperature dependence on rectifying and photoelectronic properties of La_0.67Sr_0.33MnO₃/Nb:SrTiO₃（LSMO/STON） junctions with the thickness values of LSMO film varying from 1 nm to 54 nm are systematically studied. As shown experimentally, the junctions exhibit good rectifying properties. The significant differences in photoemission property among the LSMO/STON junctions are observed. For the junction in a thicker LSMO film, the photocurrent shows a mono... 