Force-sensitive properties of FeCuNbSiB powder/silicone rubb
发布时间：2023-05-04 02:35
Composite films of different contents were prepared by Fe73.5Cu1Nb3Si13.5B9 powder as compound phase and silicone rubber as matrix phase.The thickness of film is 200 um.Values of impedance,Z,under pressure stress were measured by TH2816 LCR digital bridge.LYYL-500 N high-grade-type microcomputer control pressure testing machine was used to conduct program control loading with a speed of 0.1 mm·min-1.The results show that composite...
【文章页数】：6 页
【文章目录】：
1 Introduction
2 Experimental
3 Results and discussion
3.1 Microstructural analysis and magnetic properties of composite films
3.2 Force-sensitive properties of composite films
3.3 Influence of frequency on force-sensitive properties
3.4 Influence of powder heat treatment on force-sensitive properties
4 Conclusion
本文编号：3807778
【文章页数】：6 页
【文章目录】：
1 Introduction
2 Experimental
3 Results and discussion
3.1 Microstructural analysis and magnetic properties of composite films
3.2 Force-sensitive properties of composite films
3.3 Influence of frequency on force-sensitive properties
3.4 Influence of powder heat treatment on force-sensitive properties
4 Conclusion
本文编号：3807778
本文链接：https://www.wllwen.com/guanlilunwen/gongchengguanli/3807778.html