常用木板材料的燃烧特性研究

发布时间：2018-03-18 00:21

  本文选题：木材　切入点：燃烧特性　出处：《消防科学与技术》2016年09期 　论文类型：期刊论文

【摘要】：基于ISO 5660标准,利用锥形量热仪对白蜡木、黑胡木、红橡木和榉木在外加辐射热通量为25、35、50kW/m2的条件下进行了燃烧实验,对比分析了4种材料在不同辐射热通量下的热释放速率(HRR)、总释放热(THR)、质量损失(ML)、燃烧热(HOC)和有效燃烧热(EHC)。结果表明不同木材的(HRR)都有两个峰值,都有升温、着火、加剧、过渡和熄火5个阶段;总释放热为6~7 MJ/m3;ML曲线规律基本相同,残炭量为15%~25%;燃烧热为9.0 MJ/kg、有效燃烧热约11.5MJ/kg。
[Abstract]:Based on ISO 5660 standard, the combustion experiments of white wax wood, black Hu wood, red oak and beech were carried out under the condition of external radiant heat flux of 25 ~ 35 ~ 50 kW / m ~ 2 by using a cone calorimeter. The heat release rate (HRR), total heat release (THR), mass loss (MLN), combustion heat (HCC) and effective combustion heat (EHC) of the four materials under different radiant heat fluxes are compared and analyzed. The results show that there are two peaks in the heat release rate of different wood, which are temperature rise, ignition and aggravation. The total heat of release is 67 MJ / m3ML, the residual carbon is 15 and 25, the heat of combustion is 9.0 MJ / kg, and the effective combustion heat is about 11.5 MJ / kg.
【作者单位】： 中国科学技术大学火灾科学国家重点实验室;
【基金】：国家自然科学基金专项基金资助项目(51323010) 中央高校基本科研业务费专项资金资助项目(WK2320000034)
【分类号】：TU564

【相似文献】

相关期刊论文 前10条

1 安翠;魏东;胡小康;胡菲菲;;低压(低氧)条件下古建筑装饰性织物燃烧特性的实验研究[J];热科学与技术;2010年04期

2 黄亚东;冯丹丹;吴珂;敖文;黄志义;;沥青燃烧特性的实验研究[J];消防科学与技术;2011年06期

3 沈宏辉;傅福华;;液化石油气混空气的燃烧特性分析[J];公用科技;1998年04期

4 刘瑞芝;钱秋兰;白波;陶从喜;彭学平;;水泥工业中煤的燃烧特性评价方法[J];水泥技术;2008年03期

5 关军;李念平;李新华;龙娟;刘倩;;某化纤厂通风系统聚积物的实测及燃烧特性研究[J];中国粉体技术;2006年05期

6 高春梅,邵震宇;燃气组分改变对燃烧器具燃烧特性的影响[J];煤气与热力;2000年05期

7 华敏;殷志平;潘仁明;;单室火灾的燃烧特性[J];南京工业大学学报(自然科学版);2012年02期

8 李俊毅;朱国庆;李梦媛;刘康;王昌军;;典型木竹地板燃烧特性实验研究[J];消防科学与技术;2014年04期

9 ;ASTM E84-13a建筑材料表面燃烧特性的标准试验方法[J];核标准计量与质量;2013年04期

10 王磊;;典型胶合板燃烧特性的锥形量热仪分析[J];中国公共安全(学术版);2010年04期

相关会议论文 前1条

1 马保国;王耀城;穆松;袁龙;;稻壳燃烧特性对多孔材料烧成工艺的影响[A];2008全国功能材料科技与产业高层论坛论文集[C];2008年

相关博士学位论文 前2条

1 谭福太;秸秆建材燃烧特性及生命周期研究[D];华南理工大学;2013年

2 赵威风;狭长空间油池火燃烧特性的实验与数值模拟研究[D];中国科学技术大学;2013年

，

本文编号：1627162