水灰比对珊瑚礁混凝土抗压强度影响分析

发布时间：2018-05-23 12:06

  本文选题：混凝土 + 珊瑚礁混凝土　； 参考：《施工技术》2016年23期

【摘要】：采用珊瑚石、珊瑚砂分别替代普通碎石、河砂配制珊瑚礁混凝土,通过对6组水灰比为0.50~0.27的珊瑚礁混凝土不同龄期的强度试验,分析了水灰比、养护龄期对珊瑚礁混凝土抗压强度的影响。研究表明:珊瑚礁混凝土抗压强度随水灰比的降低而提高,当水灰比0.40时,伴随水灰比的降低珊瑚礁混凝土强度提高幅度显著低于普通混凝土;珊瑚礁混凝土抗压强度与水灰比可用二阶多项式表示。
[Abstract]:Coral reef concrete was prepared with coral reef stone and coral sand instead of ordinary gravel. The water cement ratio of 6 groups of coral reef concrete with water / cement ratio of 0.50 to 0.27 was analyzed through the strength tests of coral reef concrete at different ages. Effect of curing age on compressive strength of coral reef concrete. The results show that the compressive strength of coral reef concrete increases with the decrease of water-cement ratio, and when the water-cement ratio is 0.40, the increase range of coral-reef concrete strength with water-cement ratio is significantly lower than that of ordinary concrete. The compressive strength and water cement ratio of coral reef concrete can be expressed by second order polynomial.
【作者单位】： 水工构造物耐久性技术交通运输行业重点实验室;
【分类号】：TU528

【相似文献】

相关期刊论文 前8条

1 于红兵;孙宗勋;唐诚;;南沙群岛珊瑚砂物理力学性质研究(英文)[J];Marine Science Bulletin;2006年02期

2 叶海民;周辉;钟小帅;;中国南海某珊瑚砂岛动力环境分析[J];土工基础;2013年05期

3 卢博,李起光,黄韶健;海水—珊瑚砂屑混凝土的研究与实践[J];广东建材;1997年04期

4 程忠庆;阳平;姜海波;;珊瑚砂中浅基础抗风可靠性动态分析[J];水电能源科学;2014年07期

5 张梅英,袁建新,杨育文,曾立波;珊瑚砂土在加载过程中颗粒滑移与孔隙分维变化特征[J];岩土力学;1998年04期

6 程忠庆;阳平;姜海波;;珊瑚砂环境中方形基础地基沉降量计算方法[J];水电能源科学;2013年04期

7 马炳辰,付增祥;“高喷”注浆技术在地下集水池封底工程中的应用[J];中州煤炭;1993年06期

8 ;[J];;年期

相关会议论文 前2条

1 王艳红;陆培东;曾成杰;;西沙群岛珊瑚砂运动特性试验研究[A];第十六届中国海洋（岸）工程学术讨论会（下册）[C];2013年

2 潘柏州;韦灼彬;;原材料对珊瑚砂混凝土抗压强度影响的试验研究[A];第23届全国结构工程学术会议论文集（第Ⅲ册）[C];2014年

相关硕士学位论文 前1条

1 曾成杰;珊瑚砂运动特性及珊瑚砂岛泥沙流失防治研究[D];南京水利科学研究院;2009年

，

本文编号：1924658