PVAc对MMA基混凝土修补材料收缩性能的影响

发布时间：2019-03-30 15:26

【摘要】：针对MMA基混凝土修补材料固化时的高收缩性,研究了低收缩剂PVAc对MMA基混凝土修补材料固化收缩的改善作用。采用红外光谱分析(IR)、扫描电镜分析(SEM)、体积收缩和黏结强度实验对改性修补材料进行了结构和性能分析。结果表明:当PVAc树脂溶液掺量为12%时,MMA基混凝土修补材料的体积收缩率最低,为3.5%;改性修补材料黏结强度最高达到4.8 MPa,断裂面产生在砂浆试件内部。阐述了低收缩添加剂减缩机理,PVAc颗粒在修补材料固化时,周围产生微孔隙,从而减少固化收缩。
[Abstract]:Aiming at the high shrinkage of MMA-based concrete repair material, the effect of low shrinkage agent PVAc on the curing shrinkage of MMA-based concrete repair material was studied. Infrared spectroscopy (IR),) was used to analyze the volume shrinkage and bonding strength of (SEM),. The structure and properties of the modified repair material were analyzed. The results show that when the content of PVAc resin solution is 12%, the volume shrinkage of MMA-based concrete repair material is the lowest, 3.5%, and the adhesive strength of modified repair material is up to 4.8 MPa, fracture surface, which is produced in the interior of mortar test piece. The mechanism of reducing shrinkage of low shrinkage additive was described. When PVAc particles were cured, micropores were produced around them, thus reducing curing shrinkage.
【作者单位】： 南京工业大学材料科学与工程学院国家江苏先进生物与化学制造协同创新中心;
【分类号】：TU578

【参考文献】

相关期刊论文 前3条

1 杨志伟;徐玲玲;;MMA基混凝土修补材料的改性[J];南京工业大学学报(自然科学版);2010年05期

2 李钟宝;蔡晨露;刘秀梅;;邻苯二甲酸酯类增塑剂合成与应用研究进展[J];塑料助剂;2010年04期

3 李晓,徐玲玲,邓敏;MMA基混凝土修补材料的制备与性能[J];南京工业大学学报(自然科学版);2004年01期

【共引文献】

相关期刊论文 前10条

1 徐少云;高培伟;潘金敢;张丽芳;孙亚飞;刘宏伟;陈卫峰;;地铁混凝土管片裂缝修补后抗侵蚀性能研究[J];硅酸盐通报;2016年08期

2 夏庆兵;王军;朱鲁生;王金花;刘文军;;土壤微生物对邻苯二甲酸二(2-乙基己)酯胁迫的生态响应[J];农业环境科学学报;2016年07期

3 刘艳杰;丁斌;金朝辉;郝凤岭;关昶;李祥;刘群;王海东;;活性白土催化合成三甘醇二异辛酸酯[J];化学世界;2016年03期

4 王昱文;柴淼;曾甯;唐阵武;;典型废旧塑料处置地土壤中邻苯二甲酸酯污染特征及健康风险[J];环境化学;2016年02期

5 王振军;刘亮;邵明玉;徐智新;周琳琳;;水泥混凝土路面板底补强材料的流动性能[J];公路;2015年09期

6 张小娜;温中华;;基于缺陷修补的膨胀纤维混凝土耐久性研究[J];人民黄河;2015年08期

7 付世达;孙洋;郑森森;于晓颖;;管道修补剂的研究现状[J];中国粉体工业;2015年01期

8 徐皓;唐莹;司冠儒;吴锋;宋郸;张庄英;张欢;张温清;周萍;;白酒中塑化剂检测方法的分析研究[J];酿酒;2015年01期

9 李志莹;蒋平平;楚U，

本文编号：2450202