电子束选区熔化成形角度对TC4合金组织的影响

发布时间：2018-01-10 11:28

本文关键词：电子束选区熔化成形角度对TC4合金组织的影响　出处：《热加工工艺》2017年18期 　论文类型：期刊论文

【摘要】：利用电子束选区熔化技术制备90°、60°、30°和0°的7 mm TC4钛合金试样板,研究了成形角度对显微组织的影响。结果表明:电子束选区熔化制备的试样具有平行于扫描方向的层带组织;90°、60°和30°试样中的β柱状晶贯穿多个层带,其主轴平行于粉末沉积方向,β柱状晶内针状马氏体α'相互交错形成网篮状魏氏组织,β柱状晶和马氏体α'的宽度随成形角度减小而增大;成形角度为0°的试样组织为细长的β晶粒,β晶内α相平行分布形成α集束,各β晶粒中的α集束取向不同。
[Abstract]:Electron beam selective melting technique was used to fabricate 7mm TC4 titanium alloy samples with 90 掳~ 60 掳~ (30 掳) and 0 掳. The effect of forming angle on microstructure is studied. The results show that the sample prepared by electron beam selective melting has laminar structure parallel to the scanning direction. The 尾 columnar crystals in 90 掳60 掳and 30 掳samples run through multiple laminar zones, and their main axis is parallel to the direction of powder deposition. The acicular martensite 伪'in 尾 columnar crystals interlaced with each other to form a netlike Weiss structure. The width of 尾 columnar crystal and martensite 伪 'increases with the decrease of forming angle. When the forming angle is 0 掳, the microstructure of the sample is thin and the 伪 phase in 尾 crystal distributes parallel to form a cluster, and the orientation of 伪 cluster in each 尾 grain is different.
【作者单位】：上海工程技术大学材料工程学院;
【基金】：国家自然科学基金项目(51405288) 上海工程技术大学研究生创新项目(E3-0903-16-01048,E3-0903-16-01211)
【分类号】：TG146.23;TG661
【正文快照】： 基于粉末层的电子束选区熔化技术(Electronbeam selective manufacturing,EBSM)是一种新型的增材制造技术,电子束的作用深度较大,在真空环境下可有效地高速扫描和加热熔化预置合金粉末层,能够按照零件的截面轮廓,通过不断地逐层熔化和凝固,使金属粉末叠加,最终直接成形内部组

【相似文献】