辊速对含铬电工钢条带组织和性能的影响

发布时间：2018-01-22 18:25

  本文关键词： 电工钢条带 辊速 铬元素 熔体旋淬法　出处：《热加工工艺》2017年10期 　论文类型：期刊论文

【摘要】：利用熔体旋淬法采用不同辊速制得含Cr电工钢条带,并通过金相显微镜、XRD、显微硬度对加Cr前后的条带组织和性能进行研究。结果表明:随着辊速的增加,Fe-6.5%Si电工钢条带的组织均匀性增大,韧性增强;Cr元素可细化Fe-6.5%Si电工钢条带的晶粒尺寸,同时提高其强度和塑韧性;利用熔体旋淬法制备添加适量Cr的Fe-6.5%Si条带,并配以较高的辊速是一种可行的方法。
[Abstract]:The speed was Cr containing electrical steel strip with different roll by melt spinning method, and through optical microscope, XRD, microhardness of Cr before and after the strip microstructure and properties were studied. The results showed that with the increase of roller speed, Fe-6.5%Si electrical steel strip microstructure uniformity increases and the toughness enhancement; Cr element refinement of Fe-6.5%Si electrical steel strip with the grain size, and improve its strength and toughness; Fe-6.5%Si bands by adding appropriate amount of Cr by using melt spinning, and with high speed and is a feasible method.

【作者单位】： 潍坊科技学院汽车工程学院;
【分类号】：TM275
【正文快照】： 电工钢被广泛应用于电力行业,为我国电力事业的发展做出了极大贡献。电工钢的优异磁性能来源于其成分中的Si含量,目前常用的电工钢Si含量在4%以内,有研究表明[1-3]:当Si含量提升至6.5%,电工钢能获得最优的磁性能,但由于硅含量的增高,材料的脆性急剧增大[4],常温下根本无法采用，

本文编号：1455431