环氧沥青及其混合料性能研究

发布时间：2018-01-12 16:23

本文关键词：环氧沥青及其混合料性能研究　出处：《筑路机械与施工机械化》2015年12期 　论文类型：期刊论文

【摘要】：为了发现环氧沥青及其混合料目前存在的问题,采用宏观和微观两方面探索环氧沥青性能的大幅度改善,通过对环氧沥青的化学流变特性、固化特性以及环氧沥青混合料的抗剪性能、水损坏特性的分析归纳,得出不同组分的环氧沥青和不同地理环境对沥青性能改善各有侧重。最终结论:环氧沥青的特性是有针对性地改善其性能;深入研究环氧沥青的寿命成本及不同温度下黏弹塑性材料参数将成为重点。
[Abstract]:In order to find out the existing problems of epoxy asphalt and its mixture, this paper uses macro and micro aspects to explore the great improvement of epoxy asphalt performance, through the chemical rheological properties of epoxy asphalt. The curing characteristics, shear resistance and water damage of epoxy asphalt mixture are analyzed and summarized. It is concluded that different components of epoxy asphalt and different geographical environment have different emphasis on the performance improvement of asphalt. Finally, it is concluded that the property of epoxy asphalt is to improve its performance. It will be important to study the life cost of epoxy asphalt and the parameters of viscoelastic-plastic materials at different temperatures.
【作者单位】：长安大学教育部特殊地区公路工程重点实验室;
【基金】：国家自然科学基金(51208043) 中央高校基本科研业务费专项资金项目(0009-2014G2 210004)
【分类号】：U414
【正文快照】： 0引言环氧沥青是一种热固性聚合物材料,由组分A(环氧树脂)和组分B(含有固化剂的环氧沥青)组成。组分A和组分B在一定的条件下即开始固化反应,主要表现为环氧沥青与混合料的粘结性能随温度的升高而增大[1]。国外对环氧沥青的研究起步较早,投入了大量的人力、物力,目前技术成熟;

【共引文献】