水性环氧乳化沥青应用进展

发布时间：2018-04-25 13:43

本文选题：乳化沥青 + 水性环氧　；参考：《筑路机械与施工机械化》2017年06期

【摘要】：正0引言目前,中国主要采用SBR胶乳对乳化沥青进行改性,SBR改性沥青具有优良的高温性能、低温性能以及高黏度、难乳化的特点,但使用常规的乳化工艺乳化效果较差,难以得到稳定的改性乳化沥青~([1-2])。国内外对改性剂的使用有很多探索,其中使用水性环氧树脂改性乳化沥青(简称水性环氧乳化沥青)是较好的选择之一。水性环氧乳化沥青具有一般热固性材料的特征,固化交联后形
[Abstract]:At present, SBR latex is mainly used to modify emulsified asphalt in China. It has excellent high temperature performance, low temperature performance, high viscosity and difficult emulsification, but the emulsification effect is poor by conventional emulsification technology. It is difficult to obtain stable modified emulsified asphalt ([1-2]). There are many explorations on the use of modifiers at home and abroad, among which waterborne epoxy modified emulsified asphalt (referred to as waterborne epoxy emulsified asphalt) is one of the better choices. Waterborne epoxy emulsified asphalt has the characteristics of general thermosetting material and curing crosslinking hind shape.
【作者单位】：长安大学特殊地区公路工程教育部重点实验室;渭南市公路工程建设处;许昌华杰公路勘察设计有限责任公司;河南宏盛工程监理有限公司;
【基金】：陕西省交通运输厅科技项目(No.16-05k)
【分类号】：U414

【参考文献】