新型温拌沥青改性剂制备与性能研究

发布时间：2018-07-03 02:36

  本文选题：温拌沥青改性剂 + 基质沥青　； 参考：《化工新型材料》2017年03期

【摘要】：以苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)、C9石油树脂、硫化剂为原料制备新型温拌沥青改性剂对基质沥青进行改性,测定改性沥青的针入度、软化点、延度来探讨不同组分配合比的新型温拌沥青改性剂对基质沥青性能的影响。结果表明:新型温拌沥青改性剂中SBS、C9石油树脂和硫化剂最佳配合比为5∶3∶6,改性剂的最佳掺量为6%(wt,质量分数),最适宜的拌合温度为150℃,制得的新型温拌沥青的针入度为62.9/0.1mm、软化点为56℃、延度为130mm,黏度为0.152Pa·s,改性效果最佳。
[Abstract]:A new type of warm mix asphalt modified by styrene butadiene styrene block copolymer (SBS), C9 petroleum resin and vulcanizing agent was used as raw material to modify the matrix bitumen. The influence of the new asphalt modifier on the performance of matrix bitumen was investigated by measuring the penetration, softening point and ductility of the modified asphalt. The optimum mix ratio of SBS, C9 petroleum resin and vulcanizing agent is 5: 3: 6, the optimum dosage of the modifier is 6% (WT, mass fraction), the optimum mixing temperature is 150 C, the needle penetration of the new type of warm mix asphalt is 62.9/0.1mm, the softening point is 56, the ductility is 130mm, the viscosity is 0.152Pa s, and the modification effect is best.
【作者单位】： 武汉科技大学城市建设学院;
【基金】：湖北省自然科学基金资助(2011CDB237) 湖北省教育厅基金资助(D20121110)
【分类号】：U414

【参考文献】

相关期刊论文 前2条

1 王晓倩;陆江银;曹敏娜;;废橡胶改性沥青的储存稳定性研究[J];石油炼制与化工;2014年04期

2 李秀君,原健安,戴经梁;沥青针入度与流变特性关系[J];长安大学学报(自然科学版);2003年02期

【共引文献】

相关期刊论文 前10条

1 廖国胜;赵鹏飞;杨海波;郭胜龙;;新型温拌沥青改性剂制备与性能研究[J];化工新型材料;2017年03期

2 王瑞林;张坤;;基于液相色谱改性沥青剂量粘度和针入度测试法研究[J];公路工程;2016年02期

3 Q贸，

本文编号：2092004