高性能反应型沥青冷补液研究

发布时间：2018-07-10 01:15

  本文选题：高性能沥青冷补液 + 沥青冷补料　； 参考：《公路工程》2015年02期

【摘要】：沥青路面出现的坑槽、破损等病害影响道路的正常使用,沥青冷补料是一种全天候坑槽修补材料,能快速对这类病害进行修补。研究开发了一种高性能单组份反应型树脂预聚体沥青冷补液,通过试验优选了反应型树脂预聚体及其掺量和稀释剂种类,并通过旋转粘度试验考察了沥青冷补液储存稳定性。将本研究开发的冷补液与集料拌和制备冷补料与市售的3种冷补料对比,本冷补料能够更快的形成较高的强度,缩短养护时间。
[Abstract]:The defects of asphalt pavement, such as potholes and breakage, affect the normal use of roads. Asphalt cold filling is a kind of all-weather pothole repair material, which can be repaired quickly. A kind of high performance one-component reactive resin prepolymer bitumen cold rehydration was developed. The reactive resin prepolymer, its content and diluent were selected by experiments, and the storage stability of asphalt cold rehydration solution was investigated by rotating viscosity test. Comparing the cold rehydration developed by this study with the three kinds of cold feeders sold in the market, the cold rehydration can form higher strength and shorten the curing time.
【作者单位】： 重庆市智翔铺道技术工程有限公司;
【基金】：国家自然科学基金资助项目(51202214) 重庆市杰出青年基金资助项目(cstc2014jcyjjq30002)
【分类号】：U414

【参考文献】

相关期刊论文 前7条

1 韩继国;王选仓;时成林;崔雷;;寒区冷补沥青混合料路用性能评价指标及试验检测方法研究[J];公路;2008年05期

2 周玉利;王亚玲;颜祖兴;张幸杰;漆亮;;AH型冷补混合料的研制与施工质量控制[J];中外公路;2011年04期

3 余祖均;;冷补沥青混合料的生产和施工[J];贵州工业大学学报(自然科学版);2007年05期

4 张俊;楚好;逯艳华;武泽锋;;乳化沥青冷补料成型、养生和试验方法研究[J];中外公路;2014年04期

5 胡莉花;胡小勇;;浅析冷补沥青混合料在公路养护中的运用[J];华东公路;2008年01期

6 刘晓文;;冷补沥青混合料性能评价方法研究[J];科学技术与工程;2009年18期

7 李峰;黄颂昌;徐剑;秦永春;;冷补沥青混合料性能评价及技术要求[J];同济大学学报(自然科学版);2010年10期

【共引文献】

相关期刊论文 前10条

1 朱洪威;;冷再生混合料疲劳性能的室内试验研究[J];四川建筑科学研究;2012年02期

2 周小舟;杭莉;;浅析冷补沥青混合料在公路养护中的应用[J];公路交通科技(应用技术版);2009年06期

3 张继红;;浅谈SBS冷拌液在高等级公路日常养护中的应用[J];科技创新与应用;2012年26期

4 徐基立;潘正华;于胜军;杨锡武;;常温沥青性能及其在沥青路面养护维修中的应用研究[J];公路交通技术;2013年03期

5 yれ堪，

本文编号：2111446