低温沥青混合料抗冻性能试验研究

发布时间:2018-07-10 07:04

  本文选题:低温沥青混合料 + 抗冻性能 ; 参考:《公路工程》2017年04期


【摘要】:针对低温沥青混合料抗冻性能差问题,结合表面自由能理论对低温沥青、混合料配合比进行了设计,研究了低温沥青混合料的压实特性,并分析了沥青与集料粘附性及空隙率对抗冻性能影响。结果表明,低温沥青混合料压实特性与环境温度、击实次数具有较好的相关性;沥青与集料粘附性能有效改善混合料抗冻性能;最不利空隙率为8.3%,临界空隙率为12%;LB—13级配初始强度及抗冻性能均优于AC—13级配。
[Abstract]:Aiming at the problem of poor frost resistance of low-temperature asphalt mixture, combined with the theory of surface free energy, the compaction characteristics of low-temperature asphalt mixture are studied. The effects of adhesion of asphalt and aggregate and porosity on freezing resistance were analyzed. The results show that the compaction characteristics of low temperature asphalt mixture have good correlation with ambient temperature and compaction times, and the adhesion between asphalt and aggregate can effectively improve the frost resistance of asphalt mixture. The most unfavorable porosity is 8.3 and the critical porosity is 12% LB-13. The initial strength and frost resistance of LB-13 grade are better than that of AC-13 grade.
【作者单位】: 哈尔滨工业大学交通学院;四川省路面结构材料及养护工程试验室;四川省交通运输厅公路规划勘察设计研究院;
【基金】:“十一五”国家科技支撑计划项目(2008BAG10B02)
【分类号】:U414

【相似文献】

相关期刊论文 前4条

1 时洪顺;于丹;;公路土基抗冻性能的改善[J];黑龙江交通科技;2012年11期

2 王国忠,赵尘;沥青稳定基层混合料抗冻性能正交试验研究[J];内蒙古农业大学学报(自然科学版);2004年03期

3 杨扬;刘海苹;;寒区ATPB基层抗冻性能研究[J];黑龙江工程学院学报;2008年02期

4 韩优良;;水泥粉煤灰稳定碎石的路用性能[J];交通世界(建养.机械);2012年05期

相关硕士学位论文 前2条

1 付二全;内蒙古严寒地区水泥混凝土路面抗冻性能试验研究[D];长安大学;2015年

2 王利强;玄武岩纤维混凝土抗冻性能试验研究[D];内蒙古工业大学;2014年



本文编号:2112545

资料下载
论文发表

本文链接:https://www.wllwen.com/kejilunwen/daoluqiaoliang/2112545.html


Copyright(c)文论论文网All Rights Reserved | 网站地图 |

版权申明:资料由用户f8648***提供,本站仅收录摘要或目录,作者需要删除请E-mail邮箱bigeng88@qq.com