磁场作用下的磁流变液导电性和导热性

发布时间：2018-04-21 11:19

  本文选题：磁流变液 + 磁场　； 参考：《华南理工大学学报(自然科学版)》2014年10期

【摘要】：通过自制的实验装置,对制备的两种不同的铁钴镍磁流变液进行了实验研究,分析了其在不同磁场强度下的导电、导热规律,并与铁钴镍磁粉本身的导电性和导热性进行了对比.结果表明:在磁场作用下,铁钴镍磁流变液和铁钴镍磁粉的导电性和导热性均发生明显的变化;在磁场强度在0~0.92T内增大时,铁钴镍磁粉的电阻会有两到三个数量级的下降,其导热系数从4W/(m·K)增加到13.2W/(m·K),导热性显著提高,两种磁流变液的导热系数也均有提高.
[Abstract]:Two different kinds of ferrocobalt and nickel magnetorheological fluids were studied by a self-made experimental device. The conductivity and heat conduction of the ferrocobalt nickel magnetic powder were compared with that of the iron cobalt nickel magnetic powder. The results showed that the ferrocobalt and nickel magnetorheological fluid and the iron cobalt nickel magnetic powder were in the field of magnetic field. The conductivity and the thermal conductivity of the iron cobalt nickel magnetic powder will decrease from two to three orders of magnitude when the magnetic field strength is increased in 0~0.92T. The thermal conductivity increases from 4W/ (M. K) to 13.2W/ (M. K), the thermal conductivity is significantly improved, and the thermal conductivity of the two kinds of magnetorheological fluids is also improved.

【作者单位】： 北京理工大学机械与车辆学院;
【基金】：广东省教育部产学研结合项目(00434311220218085)
【分类号】：O441.4

【相似文献】

相关期刊论文 前10条

1 李发胜;张平;;抛光用磁流变液的研究[J];功能材料;2006年08期

2 陈伟俊;马平;;磁流变液的抗沉淀分析[J];机床与液压;2007年10期

3 裴畅贵;郭张霞;;磁流变液特性分析[J];机械管理开发;2007年02期

4 于广泽;刘纪元;史庆藩;;磁流变液演示仪[J];物理实验;2010年06期

5 廖昌荣;王可俐;张红辉;董小闵;余淼;陈伟民;;基于正弦激励的磁流变液非稳态环状流动特性研究[J];中国矿业大学学报;2006年04期

6 潘胜,吴建耀,胡林,沈峰,孙猛,周鲁卫;磁流变液的屈服应力与温度效应[J];功能材料;1997年03期

7 李海涛;彭向和;黄尚廉;;基于偶极子理论的磁流变液链化机理模拟研究[J];功能材料;2008年06期

8 胡林;张朝平;;明胶-氧化铁磁流变液的制备及性能[J];机械工程材料;2006年07期

9 李长江;王治国;王金刚;;纳米Fe_3O_4加入量对磁流变液性能的影响[J];磁性材料及器件;2009年04期

10 邓益民;叶伟强;王威;;基于磁流变弹性体导电机理的压阻特性理论模型研究[J];机械制造;2011年05期

，

本文编号：1782232