含能黏合剂3-硝酸酯甲基-3-甲基氧丁环聚合物的固化体系研究

发布时间：2017-12-26 19:18

本文关键词：含能黏合剂3-硝酸酯甲基-3-甲基氧丁环聚合物的固化体系研究　出处：《兵工学报》2016年08期 　论文类型：期刊论文

【摘要】：采用Materials Studio分子模拟软件对3-硝酸酯甲基-3-甲基氧丁环聚合物(Poly NIMMO)与甲苯二异氰酸酯(TDI)、异佛尔酮二异氰酸酯(IPDI)和六次甲基二异氰酸酯和水的加成物(N-100)3种固化剂形成的混合体系固化行为及弹性模量进行了理论模拟,并与固化胶片力学性能实测数据进行了对比分析,研究了含能黏合剂Poly NIMMO的固化体系。结果表明:TDI、IPDI和N-100 3种固化剂均可与含能黏合剂发生聚氨酯交联反应,形成稳定的固化体系;与Poly NIMMO匹配的固化剂,以N-100为最佳,固化催化剂则以二月桂酸二丁基锡为最佳,最终形成的固化胶片力学性能为最大抗拉强度3.83 MPa,最大延伸率282%.
[Abstract]:Using Materials Studio molecular simulation software of 3- nitrate -3- methyl oxetane polymer (Poly NIMMO) and toluene diisocyanate (TDI), isophorone diisocyanate (IPDI) and six methylene diisocyanate and water adduct (N-100) of 3 kinds of curing agent into the mixture system of curing behavior and elastic modulus were the theoretical simulation, and compared with the measured data of mechanical properties of the cured film, energetic curing adhesive system NIMMO Poly. The results showed that TDI, IPDI and N-100 3 kinds of curing agent and energetic binder can occur polyurethane crosslinking reaction, the formation of a stable curing system; curing agent, and Poly NIMMO, to N-100, the curing catalyst two lauric acid two butyl tin is the best curing film mechanical properties of the final form of the maximum tensile the intensity of 3.83 MPa, the elongation rate of 282%.
【作者单位】：西安近代化学研究所;陕西师范大学化学化工学院;
【基金】：国家自然科学基金项目(21401124) 陕西省科技计划项目(2013KJXX-43)
【分类号】：V512
【正文快照】： 0引言纵观固体推进剂的发展历程,每一种新型推进剂的出现、推进剂综合性能的提高都离不开新型黏合剂的应用,如硝化纤维素(NC)、沥青、聚硫橡胶(PS)、端羟基聚丁二烯(HTPB)、聚乙二醇(PEG)等。HTPB、PEG等是迄今为止复合推进剂和高能硝酸酯增塑聚醚(NEPE)推进剂中综合性能最好

【相似文献】