含有纳米铝颗粒的高密度悬浮燃料研究

发布时间：2018-01-20 05:15

  本文关键词： 应用化学 高密度燃料 含能纳米颗粒 推进剂 悬浮燃料　出处：《推进技术》2016年05期 　论文类型：期刊论文

【摘要】：铝颗粒是一种高密度高能量的燃料添加剂,研究了一条通过表面改性使纳米铝颗粒分散在液体碳氢燃料中,进而制备高密度悬浮燃料的路线。采用三正辛基氧膦对铝颗粒进行表面改性,表征了改性颗粒的结构和在燃料中的分散稳定性,测试了悬浮燃料的密度、能量和粘度。结果表明,表面改性能够阻止铝颗粒的团聚和沉降,使其较长时间内稳定分散在高密度燃料HD-03中;含有铝颗粒的悬浮燃料的密度和体积热值显著提高,保持液体状态和良好流动性。其中,含有10wt%和30wt%铝颗粒时的燃料密度分别为1.06g/m L,1.14g/m L,体积能量分别为44.3MJ/L,45.4MJ/L,动力粘度分别为80m Pa·s,2000m Pa·s。
[Abstract]:Aluminum particle is a kind of fuel additive with high density and high energy. The surface modification of aluminum particles with trioctylphosphine oxide was carried out, the structure of the modified particles and the dispersion stability in the fuel were characterized, and the density of the suspended fuel was tested. The results show that the surface modification can prevent the agglomeration and sedimentation of aluminum particles and make them disperse stably in high density fuel HD-03 for a long time. The density and volume caloric value of suspended fuel containing aluminum particles are significantly increased to maintain liquid state and good fluidity. The fuel density of 10wt% and 30wt% aluminum particles is 1.14g / mL and the volumetric energy is 44.3 MJ / L and 45.4 MJ / L, respectively. The dynamic viscosity is 80 MPA 路s ~ (2 000) MPA 路s ~ (-1).
【作者单位】： 天津大学化工学院先进燃料与化学推进剂教育部重点实验室天津化学化工协同创新中心;
【基金】：装备预研项目(625010304)
【分类号】：V51
【正文快照】： 1引言液体碳氢燃料在航天推进领域占有重要地位,燃料性能(尤其是能量和密度)是决定飞行性能(包括航程、航速和有效载荷等)的关键之一。高性能飞行器的发展对燃料的推进能力提出了更高的要求,高密度燃料具有更大的质量密度和体积热值,可以在不增加燃料箱尺寸的情况下提供更多的，

本文编号：1446990