水泥砂浆受硫酸钠侵蚀时力学特性的尺寸效应研究

发布时间：2019-02-17 13:36

【摘要】：为了解水泥砂浆试件经海水侵蚀时的尺寸效应,分别采用3种尺寸的正方体试件放在硫酸钠溶液中侵蚀,后每隔一定时间取出部分试件进行单轴压缩试验,分析不同尺寸试件的单轴抗压强度、峰值应变和弹性模量的差异。研究结果表明:试件经硫酸钠侵蚀时强度的尺寸效应存在一个临界值,随着试件尺寸的增加,侵蚀对强度的影响效应会呈现增加后减小的规律;不同尺寸的试件经硫酸钠侵蚀时,其峰值应变和弹性模量的差异没有强度的差异明显。
[Abstract]:In order to understand the size effect of cement mortar specimen under seawater erosion, three kinds of cuboid specimens were used to erode in sodium sulfate solution, and some specimens were taken out every certain time for uniaxial compression test. The difference of uniaxial compressive strength, peak strain and elastic modulus of specimens with different sizes is analyzed. The results show that there is a critical value of the size effect of the strength when the specimen is corroded by sodium sulfate. With the increase of the size of the specimen, the effect of erosion on the strength will be increased and then decreased. The difference of peak strain and elastic modulus of specimens with different sizes was not obvious when the specimen was eroded by sodium sulfate.
【作者单位】： 中国电建集团中南勘测设计研究院有限公司水能资源利用关键技术湖南省重点实验室;成都理工大学地质灾害防治与地质环境保护国家重点实验室;宁波大学建筑工程与环境学院;武汉地铁集团有限公司;
【基金】：水能资源利用关键技术湖南省重点实验室开放研究基金项目(PKLHD201405)
【分类号】：TQ177.62

【相似文献】

相关期刊论文 前10条

1 高德昊;李诗兰;;混凝土与碾压混凝土断裂尺寸效应的研究进展[J];机电产品开发与创新;2011年02期

2 李文成;钢的尺寸效应对机械设备加工质量与寿命的影响[J];流体工程;1986年08期

3 王向东;王跃锋;华曦;岑家全;;基于灰色理论的混凝土压缩损伤参数尺寸效应[J];水利水电科技进展;2011年03期

4 王兵锋;汤国庆;唐腾飞;;混凝土尺寸效应研究[J];低温建筑技术;2014年06期

5 苏捷;方志;杨钻;;骨料组分和强度等级对混凝土单轴受压性能尺寸效应的影响[J];建筑结构学报;2014年05期

6 周青松;于清树;冯本秀;;混凝土强度尺寸效应研究[J];矿业快报;2006年06期

7 陈海彬;王星原;周濵;;高强预拌混凝土尺寸效应的研究[J];混凝土;2013年09期

8 吴秋兰;童谷生;刘永胜;;BFRP约束钢筋混凝土圆柱强度尺寸效应的模拟分析[J];混凝土;2011年06期

9 张建;金龙;丁宁;;三级配混凝土静动态弯拉强度尺寸效应试验研究[J];山西建筑;2013年25期

10 张莹;张小波;;尺寸效应在大掺量活性掺合料混凝土抗碳化性能研究中的影响[J];兰州文理学院学报(自然科学版);2014年03期

相关博士学位论文 前2条

1 苏捷;混凝土受压与受拉性能的尺寸效应研究[D];湖南大学;2013年

2 方焯;BaTiO_3陶瓷晶粒结构及尺寸效应的理论研究[D];华中科技大学;2010年

相关硕士学位论文 前2条

1 陈建祥;耐火材料断裂参数尺寸效应的研究[D];辽宁科技大学;2016年

2 曹亮;考虑过程区的混凝土断裂韧度尺寸效应研究[D];河海大学;2006年

，

本文编号：2425217