文献名称：铝合金筒段化学铣切工艺研究

    前言：对2219铝合金筒段的化学铣切工艺进行了研究,以确定化学铣切工艺的最佳配方和工艺控制要点。对NaOH、Na2S、三乙醇胺(TEA)和溶解Al正交试验的结果进行了验证性试验,确定了对化学铣切表面粗糙度的影响程度依次为:Na2S、溶解Al、TEA、NaOH,化学铣切溶液的最佳配方为:75~150g/LNaOH,6~15g/LNa2S,38.5~42.0g/LTEA,溶解Al32.5~120·0g/L。按该配方对2219铝合金筒段进行化学铣切,可达到最佳效果:表面粗糙度1.2~1.4μm、化学铣切壁厚公差≤0·12mm、化学铣切轮廓线线偏离≤0·75mm。
    The chemical milling process for 2219 aluminum alloy tube was investigated using orthogonal test and the optimum formula and technology were established. It was found that the effect of various chemicals on the surface roughness of the chemically milled Al[LL] alloy was ranked as Na_2S>dissolved aluminum>triethanolamine (TEA)>NaOH. The optimum composition of the chemical milling solution was suggested as 75~150 g/L NaOH, 6~15 g/L Na_2S, 38.5~42.0 g/L TEA, and 32.5~120.0 g/L dissolved aluminum. It was able t...

文献名称 铝合金筒段化学铣切工艺研究

Article Name
英文(英语)翻译 Chemical Milling Process for 2219 Aluminum Alloy Tube;

作者 尹茂生; 廖广其; 文庆杰; 程红霞;

Author YIN Mao-sheng~1;2;LIAO Guang-qi~1;WEN Qing-jie~2;CHENG Hong-xia~2（1. School of Materials Science and Engineering;Northwestern Polytechnical University;Xi′an 710072;2. Chengdu Aircraft Industrial Company;Chengdu 610092;China）;

作者单位
Author Agencies 西北工业大学材料学院; 成都飞机工业公司热表中心工艺组; 成都飞机工业公司热表中心工艺组 陕西西安; 四川成都; 陕西西安;

文献出处
Article From 中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度

关键词 化学铣切; 2219铝合金; 表面粗糙度;

Keywords chemical milling;aluminum alloy;surface roughness;

化学铣切槽液中Na_2S的分析
钛离子含量对钛合金化学铣切的影响
机械加工中的化学铣切
新一代铝合金化学铣切保护涂料的研制
化学铣切工艺在15-5PH精密机械零件加工中的研究与应用
热塑弹性体铝合金化学铣切保护涂料的研制
铝合金的化学铣切加工
LY16铝合金的化学铣切
GH3044高温合金化学铣切工艺及其应用
无氰四元合金浸锌液中金属离子对铝合金浸锌的影响

  本文关键词：铝合金筒段化学铣切工艺研究，由笔耕文化传播整理发布。