水化热抑制剂对大体积混凝土性能的影响研究

发布时间：2018-03-01 12:28

  本文关键词： 水化热抑制剂 绝热温升 裂缝控制　出处：《建筑技术》2017年10期 　论文类型：期刊论文

【摘要】：将两种不同品种水化热抑制剂用于大体积混凝土中,模拟研究实际生产中不同掺量的水化热抑制剂对大体积混凝土绝热温升、最高温度、力学性能及工作性能的影响,结果表明与空白试件对比,两种水化热抑制剂不同掺量条件下都能在一定程度上降低混凝土的绝热温升,对大体积混凝土的内部最高温度及裂缝控制起积极作用;随水化热抑制剂掺量增加,早期强度对比空白样品偏低,但28d及60d强度稍有增长。
[Abstract]:Two kinds of hydration heat inhibitors were used in mass concrete to simulate the effects of different amount of hydration heat inhibitors on the adiabatic temperature, maximum temperature, mechanical properties and working performance of mass concrete. The results show that the two hydration heat inhibitors can reduce the adiabatic temperature rise of concrete to a certain extent, and play an active role in controlling the internal maximum temperature and crack of mass concrete. With the increase of hydration heat inhibitor content, the early strength of the sample was lower than that of the blank sample, but the strength of 28 d and 60 d increased slightly.
【作者单位】： 北京建工新型建材有限责任公司;北京建工集团第四建筑工程公司;
【分类号】：TU528

【相似文献】

相关期刊论文 前10条

1 尚建丽;杨大平;;高性能大体积混凝土逐时温度场有限元动态分析[J];四川建筑科学研究;2006年02期

2 黄允宝;刘建忠;毛永琳;;大体积混凝土的配合比设计及其工程应用[J];江苏建筑;2006年02期

3 周双喜;荣茂阁;左晟;杨雷;郑惠英;吴坤鑫;熊超琴;杨明;;复合相变储能材料在大体积混凝土中的控温性能[J];华东交通大学学报;2013年04期

4 ;用“推算法”求得水泥七天水化热[J];水泥;1979年05期

5 赵丽君;王嘉杨;;浅析原材料对大体积混凝土性能的影响[J];福建建材;2006年01期

6 马井娟;张春鹏;袁少华;;粉煤灰在大体积混凝土中的应用[J];低温建筑技术;2006年03期

7 陈铭喜;;大掺量粉煤灰在大体积混凝土中的应用[J];广东建材;2012年08期

8 赵金贵;周金光;李兰波;;某工程中大体积混凝土试验中特殊现象的启示[J];山西建筑;2012年28期

9 蒙二虎;陈备战;郎剑雷;;大体积混凝土的配合比设计及试验研究[J];粉煤灰;2012年03期

10 赵平;;现浇大体积混凝土结构工程对原材料要求分析[J];铜陵学院学报;2006年01期

相关会议论文 前2条

1 徐兆全;;大体积混凝土早期应变监测研究[A];第21届全国结构工程学术会议论文集第Ⅱ册[C];2012年

2 尹冬梅;朱广祥;江守恒;单星本;文婧;朱卫中;;LNC-53泵送型防冻剂在大体积混凝土冬期施工中的应用[A];纪念中国混凝土外加剂协会成立20周年——混凝土外加剂新技术发展研讨会论文集[C];2006年

相关博士学位论文 前1条

1 杨和礼;原材料对基础大体积混凝土裂缝的影响与控制[D];武汉大学;2004年

相关硕士学位论文 前3条

1 杨翔;瑞安天地大厦二期筏板大体积混凝土的质量检测与控制[D];重庆大学;2013年

2 冯孝杰;大体积混凝土软化曲线的新确定方法[D];浙江工业大学;2012年

3 宋伟;相变材料在大体积混凝土中的试验研究[D];北京市市政工程研究院;2012年

，

本文编号：1551933