乐启炽,欧鹏,吴跃东,路贵民,崔建忠,邱竹贤,AZ91D镁合金近液相线铸造研究

  本文关键词：AZ91D镁合金近液相线铸造研究，由笔耕文化传播整理发布。

首页 > 专家 > 内容

文献名称：AZ91D镁合金近液相线铸造研究

    前言：采用近液相线铸造的方法浇铸了镁合金 ＡＺ９１Ｄ，并与液相铸造的组织进行了对比。通过不同铸模浇铸考察厂冷却速率对组织的影响，研究了近液相线铸造时的静置时间对铸造组织的影响。实验结果表明，液相（６００℃）铸造组织与常规铸造组织接近，高冷却速率促进了枝晶化：近液相线铸造方法有利于组织的细化和球化，但下如铝合金旋著：增加冷却速率有利于组织的细化，也促进了球化的趋势，并对近液相线组织的演变机理进行了初步探讨。
    The near-liquidus casting process was used in casting AZ91D alloy, and its microstruc- ture was compared with that prepared by liquid casting. The effects of cooling rate in casting process and the holding time in near-liquidus on rnicrostructure were also observed. The results indicate that the microstructure obtained from liquid casting is similar to that of conventional casting, and den- driticization is promoted at higher cooling rate. On the contrary, near liquidus casting is beneficial to refinin...

文献名称 AZ91D镁合金近液相线铸造研究

Article Name
英文(英语)翻译 STUDY ON THE NEAR-LIQUIDUS CASTING OF AZ91D MAGNESIUM ALLOY;

作者 乐启炽; 欧鹏; 吴跃东; 路贵民; 崔建忠; 邱竹贤;

Author LE Qichi;OU Peng;WU Yuedong;LU Guimin;CUI Jianzhong;QIU Zhuxian （The Key Laboratory of Electromagnetic Processing of Materials;Ministry of Education;Northeastern University;Shenyang 110004）;

作者单位
Author Agencies 东北大学材料电磁过程研究教育部重点实验室; 东北大学材料电磁过程研究教育部重点实验室 沈阳11000;

文献出处
Article From 中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度

关键词 镁合金; 近液相线铸造; 微观组织;

Keywords magnesium alloy;near-liquidus casting;niicrostructure;

镁合金低压恒流阳极氧化膜研究
镁合金上二步法电镀锌的研究
镁合金表面化学转化膜的研究进展
累积叠轧工艺对AZ31镁合金板材组织和性能的影响
Mg-9Sr中间合金的组织及其对AZ31镁合金组织细化的影响
ZAC843镁合金金属型铸造组织和力学性能
AZ91D镁合金表面机械研磨处理后显微结构研究
pH值对AZ 91D镁合金化学镀镍的影响
AZ 31镁合金稀土转化成膜及其耐蚀性能的研究
镁合金化学镀Ni-P合金工艺研究现状

  本文关键词：AZ91D镁合金近液相线铸造研究，，由笔耕文化传播整理发布。