    前言：采用低频电磁铸造技术(电磁场频率为25Hz,安匝数12800AT),按照不同的铸造工艺参数半连续铸造制备了直径为0.1m的超高强度Al12%Zn2.5%Mg2.5%Cu0.15%Zr合金锭坯,考察了铸造温度、铸造速度和冷却水强度对铸锭组织的影响。结果表明,铸造温度为710℃,铸造速度为100mm/min,冷却水强度为0.05m3/min时的低频半连续铸锭组织均匀细小,呈现近球形,边部和中间部位的晶粒大小差别较小,其平均晶粒尺寸分别为28μm和29μm。
    Under the low frequency electromagnetic field(electromagnetic frequency is 25 Hz and ampere turns is 12 800 AT), super-high strength Al-12%Zn-2.5%Mg-2.5%Cu-0.15%Zr alloy is semi-continuously cast into ingots which are 0.1 mm in diameter. The effects of casting temperature, casting speed and intensity of cooling water on microstructure are investigated. The results show that when the casting temperature, casting speed and intensity of cooling water are 710 ℃, 100 mm/min, 0.05 m 3/min respectively, the micros...

文献名称 铸造工艺参数对超高强铝合金低频电磁半连续铸锭微观组织的影响

Article Name
英文(英语)翻译 Effects of Casting Technological Parameters on the Microstructures of Low Frequency Semi-continuously Electromagnetic Casting Alumnium Alloy Ingots with Super-high Strength;

作者 左玉波; 董杰; 崔建忠;

Author ZUO Yu-bo;DONG Jie;CUI Jian-zhong（The Key Lab of Electromagnetic Processing of Materials;Ministry of Education;Northeastern University;Shenyang 110004;Liaoning;China）;

作者单位
Author Agencies 东北大学材料电磁过程研究教育部重点实验室; 东北大学材料电磁过程研究教育部重点实验室 辽宁沈阳; 辽宁沈阳;

文献出处
Article From 中国科学院上海冶金研究所; 材料物理与化学(专业) 博士论文 2000年度

关键词 低频电磁半连续铸造; 微观组织; 铸造温度; 铸造速度; 冷却强度; Al-Zn Mg-Cu-Zr;

Keywords low frequency semi-continuously electromagnetic casting;microstructure;casting temperature;casting speed;intensity of cooling water;Al-Zn-Mg-Cu-Zr;

低频电磁半连续铸造对4045合金显微组织与性能的影响
低频电磁半连续铸造铝合金工艺及理论研究
微量Sc元素对AZ91镁合金组织性能的影响
模拟实际工况条件下高锰钢加工硬化能力的研究
镍基单晶高温合金γ和γ′相合金元素分布特征
WC颗粒增强Cr系白口铸铁复合材料的三体磨损性能的研究
新型半固态用铝合金的触变成形研究
发泡模具射料充填过程的数值模拟
结晶器电磁制动钢液流场数值模拟
专家系统在水平连铸工艺参数优化设置中的研究与应用

  本文关键词：铸造工艺参数对超高强铝合金低频电磁半连续铸锭微观组织的影响，由笔耕文化传播整理发布。