低压铸造铝合金轮毂模具保温涂料附着力的改进

发布时间：2018-11-28 15:18

【摘要】：针对铝合金轮毂低压铸造过程中由于模具涂料组成不合理、结构单一、容易脱落掉块或冲刷变薄甚至造成模具裸露,在全面分析现有涂料成分基础上,给出了改进措施。通过调整涂料组成并向其中引入晶须组分,结合适当的喷涂工艺,使铝合金轮毂低压铸造用保温涂料的使用效果得到明显改善,提高了轮毂成品率,降低了生产成本,有效提高了生产效率。
[Abstract]:In the process of aluminum alloy hub low pressure casting, due to the unreasonable composition of die coating and single structure, it is easy to fall off the block or become thin or even cause the die exposed. On the basis of comprehensive analysis of the existing coating composition, the improvement measures are put forward. By adjusting the composition of the coating and introducing whisker into it, combined with the proper spraying process, the application effect of heat preservation coating for aluminum alloy hub low pressure casting has been improved obviously, the finished product rate of the wheel hub has been increased, and the production cost has been reduced. The production efficiency is improved effectively.
【作者单位】： 辽宁科技大学高温材料与镁资源工程学院;鞍山瑞泰高温材料有限公司;重庆中南铝合金轮毂有限公司;
【分类号】：TG249.2;TQ637

【相似文献】

相关期刊论文 前10条

1 ;海泡石基保温涂料[J];技术与市场;2002年02期

2 章柏洋;;保温涂料研究开发渐热[J];化工文摘;2003年11期

3 孙书静;新型硅酸盐复合保温涂料的生产[J];现代涂料与涂装;2004年01期

4 王勃;;保温涂料研究进展[J];黑龙江科学;2011年02期

5 ;粉状复合保温涂料[J];技术与市场;2009年11期

6 吕霞;俞成丙;张云;芮英宇;;保温涂料的研究现状及其展望[J];涂料工业;2011年03期

7 孙玉琴;赵永飞;张存信;;水性保温涂料配方的研发方向[J];现代涂料与涂装;2013年07期

8 周玲,吕纹;复合硅酸盐保温涂料的研制[J];中国建材;1991年03期

9 张宏祥;;8A-1型保温涂料在西北问世[J];化学建材;1991年02期

10 ;新型隔热节能保温涂料[J];广东化工;1992年04期

相关硕士学位论文 前5条

1 张星雨;复合硅酸盐保温涂料的研究[D];西北大学;2007年

2 辛转红;有机硅改性丙烯酸酯外墙外保温涂料的研制和性能研究[D];沈阳理工大学;2011年

3 王昭申;杂环化合物及保温涂料的合成研究[D];新疆大学;2011年

4 吕文燕;薄层保温涂料的研制及其性能研究[D];大连海事大学;2010年

5 侯旭涛;离子交联硅丙乳液外墙保温涂料的制备和性能研究[D];沈阳理工大学;2014年

，

本文编号：2363263