Evolution of Microstructure,Mechanical Properties and Corros

发布时间：2022-02-15 06:38

　　Ultrasonic vibration with different powers from 0 k W to 1.6 k W was applied during the tungsten inert gas welding-brazing of Mg/Ti.The microstructures,mechanical properties and corrosion resistance of the ultrasonic assisted tungsten inert gas（U-TIG） welded-brazed Mg/Ti joint were characterized.The results showed that,without being subjected to ultrasonic vibration,coarse columnar α-Mg grains occurred in the fusion zone of Mg/Ti joint.However,with ultrasonic power of 1.2 k W,the average grain s... 

【文章来源】：Journal of Materials Science & Technology. 2016,32(12)EISCICSCD

【文章页数】：7 页

【文章目录】：
1. Introduction
2. Materials and Methods
3. Results and Discussion
    3.1. Microstructures of brazing zone
    3.2. Microstructures of fusion welding zone
    3.3. Mechanical properties
    3.4. Corrosion behaviors
4. Conclusions


【参考文献】：
期刊论文
[1]TC4钛/5052铝异种金属激光点焊工艺特性研究[J]. 孙逸铭,张泽群,檀财旺,赵晓叶,陈波,宋晓国,冯吉才.  激光与光电子学进展. 2019(03)
[2]超声振动对高氮钢激光-电弧复合焊接接头组织与性能的影响研究[J]. 刘佳,白陈明,崔博,石岩,李忠,张宏.  机械工程学报. 2018(16)
[3]热输入对镁合金对焊接头微观组织和力学性能的影响（英文）[J]. 杨方洲,周杰,熊逸博.  Journal of Central South University. 2018(06)
[4]AZ31B/TC4填镍夹层激光-电弧对接熔化焊特性[J]. 段旭,宋刚,刘黎明.  焊接技术. 2018(04)
[5]镁/钛异种合金焊接的研究现状与展望[J]. 张泽群,张凯平,檀财旺,周利,周珍珍.  焊接. 2017(11)

博士论文
[1]ZE41镁合金薄壁铸件集成计算及制备工艺研究[D]. 付玉.大连理工大学 2019

硕士论文
[1]面向散热结构的镁/铜、镁/铝、铝/铝特种焊接工艺研究[D]. 牛田星.天津理工大学 2021
[2]复合微合金化及超声处理对ZL101铝合金组织与耐腐蚀性能的影响[D]. 董布克.合肥工业大学 2021
[3]Mg、Cu及Mg/Cu异种金属超声辅助钎焊工艺和机理研究[D]. 郎强.天津理工大学 2020
[4]振动处理工艺对铸、焊件机械性能影响研究[D]. 孟祥旗.山东大学 2018
[5]高能喷丸对同种及异种金属材料的TIG焊接接头的组织和性能的影响[D]. 孙永强.重庆大学 2018



本文编号：3626117