Effect of welding parameters on Al/Ti joint property in elec

发布时间：2023-04-26 18:46

　　The electron beam welding-brazing being used to join 5A06 Al alloy to TC4 Ti alloy decreases the formation of brittle intermetallic compound.Experiments were carried out to study the influence of electron beam welding parameters on the tensile strength of welds,based on an orthogonal test and analysis method.The welding parameters include beam current,welding speed,scanning figure,scanning frequency,figure size,beam offset and focus current.The optimum parameters for3 mm 5A06 Al alloy and 2 mm T...

【文章页数】：7 页

【文章目录】：
0 Introduction
1 Experimental materials and methods
2 Optimization design of processing parameter
    2.1 Orthogonal experiments
    2.2 Results and discussion
3 Tensile strength and fracture surface
4 Conclusions



本文编号：3802016