尺寸变化对Cu-Nb-Cu多芯复合线材微观结构及性能影响

发布时间：2018-03-20 01:03

  本文选题：集束拉拔技术　切入点：Nb管　出处：《稀有金属材料与工程》2015年04期 　论文类型：期刊论文

【摘要】：采用集束拉拔技术制备出高强高导Nb管增强Cu-Nb多芯复合线材,样品直径为Φ2.5 mm时,强度接近1.1 GPa,导电率达到74%IACS。选取不同尺寸线径(Φ3.0 mm、Φ2.7 mm、Φ2.5 mm)的复合线材,通过场发射扫描电镜测试手段表征了不同尺寸线材的芯丝形貌、Cu-Nb界面的微观结构,探讨了多尺寸条件下芯丝和界面微观组织的演变规律及特性,最后结合σ-ε曲线图和R-T曲线图,详细分析了尺寸变化所引起线材性能的演变机理。
[Abstract]:The high strength and high conductivity NB tube reinforced Cu-Nb multi-core composite wire was prepared by cluster drawing technique. When the diameter of the sample was 桅 2.5 mm, the strength was close to 1.1 GPa.The conductivity reached 74IACS.The composite wire with different sizes (桅 3.0 mm, 桅 2.7 mm, 桅 2.5 mm) was selected. The microstructure of Cu-Nb interface was characterized by means of field emission scanning electron microscopy (SEM). The evolution and characteristics of the microstructure of core wire and interface were discussed under multi-dimension conditions. Finally, the 蟽-蔚 curve and R-T curve were combined. The evolution mechanism of wire properties caused by dimension change is analyzed in detail.
【作者单位】： 西北有色金属研究院;
【基金】：国家自然科学基金资助(51031002)
【分类号】：TG359

【参考文献】

相关期刊论文 前4条

1 宁远涛;张晓辉;张婕;;大变形Cu-10Ag原位纳米纤维复合材料[J];稀有金属材料与工程;2005年12期

2 梁明;陈自力;卢亚锋;李成山;闫果;李金山;张平祥;;高强高导铜铌微观复合材料的微观结构与性能[J];稀有金属材料与工程;2009年10期

3 刘瑞蕊;周海涛;周啸;陆德平;刘克明;彭谦之;彭勇;钟芳华;;高强高导铜合金的研究现状及发展趋势[J];材料导报;2012年19期

4 李春广;孙霞光;邓胜涛;管军强;肖成举;万晓波;朱思华;李建峰;杜社军;王天成;张丰收;刘向宏;冯勇;;高场磁体用RRPNb_3Sn股线的研制[J];稀有金属材料与工程;2012年08期

【共引文献】

相关期刊论文 前10条

1 耿永红;郭迎春;张吉明;刘方方;管伟明;张昆华;;大塑性变形金属基纳米纤维复合材料制备工艺与研究现状[J];材料导报;2007年08期

2 毕莉明;刘平;陈小红;刘新宽;;形变铜基原位复合材料强化机理的研究进展[J];材料导报;2011年23期

3 宁远涛;张晓辉;吴跃军;;Cu-Ag合金原位纤维复合材料的沉淀强化效应[J];稀有金属材料与工程;2007年10期

4 耿永红;郭迎春;毕s，

本文编号：1636800