非对称板形对连续退火炉内带钢跑偏的影响

发布时间：2018-03-24 18:39

  本文选题：非对称板形　切入点：连续退火　出处：《钢铁》2015年05期

【摘要】：带有非对称板形缺陷的冷轧带钢在连续退火炉内运行时极易出现跑偏现象,尤其是单边浪的影响更为明显。为评价板形缺陷的非对称性,提出了板形不对称度评价指标,并通过对实际跑偏数据与不对称度的对比分析,发现当某段带钢的板形不对称度平均值超过0.5时,带钢极易跑偏,据此制定了连续退火生产线来料板形控制标准,实际应用后,因板形缺陷问题导致的连续退火炉内带钢跑偏断带事故次数由每年8次降至3次。
[Abstract]:Cold rolled strip with asymmetric shape defects is prone to appear deviation phenomenon in continuous annealing furnace, especially the influence of single wave. In order to evaluate the asymmetry of shape defect, the evaluation index of shape asymmetry degree is put forward. Through the comparison and analysis of the actual deviation data and the asymmetry degree, it is found that when the average value of the strip shape asymmetry degree exceeds 0.5, the strip is easy to deviate. According to this, the control standard of the strip shape coming from the continuous annealing production line is established. The number of strip breakage accidents in continuous annealing furnace is reduced from 8 times to 3 times per year.
【作者单位】： 北京科技大学机械工程学院;武汉钢铁股份有限公司冷轧薄板总厂;
【基金】：中央高校基本科研业务费专项资金资助项目(FRF-TP-14-019A2)
【分类号】：TG335.5;TG156.2

【共引文献】

相关会议论文 前4条

1 刘小波;;带钢纠偏装置分析[A];中国计量协会冶金分会2011年会论文集[C];2011年

2 刘顺心;赵志坚;赵新义;郝瑛;;冷轧连续退火机组炉内张力控制优化[A];中国计量协会冶金分会2013年会论文集[C];2013年

3 李辉;柳万鹏;;数据挖掘技术在分析连退线退火炉内带钢跑偏问题上的应用[A];中国计量协会冶金分会2014年会暨能源计量与绿色冶金论坛论文集[C];2014年

4 王利国;林森木;孙晓宇;王越;杨军荣;洪天生;陈思楠;;炉辊对带钢跑偏的影响[A];2014年全国轧钢生产技术会议文集（上）[C];2014年

相关博士学位论文 前1条

1 付卓;铝热连轧跑偏控制模型及应用研究[D];中南大学;2014年

相关硕士学位论文 前7条

1 黄媛;窄幅卷筒纸零速接纸系统分析与研究[D];北京印刷学院;2011年

2 叶玉娟;带钢连续退火瓢曲现象的研究[D];河南科技大学;2009年

3 李素娥;酸洗连轧生产线带钢的跑偏控制及仿真分析[D];中南大学;2008年

4 宋小平;连退炉加热段通板稳定技术的研究[D];东北大学;2010年

5 高轶颉;冷轧连续退火机组张力在线控制的研究[D];河北科技大学;2013年

6 孙晓宇;冷轧带钢瓢曲现象的研究与控制[D];辽宁科技大学;2014年

7 张云鹏;基于滑模变结构的带钢纠偏控制方法研究[D];东北大学;2012年

【二级参考文献】

相关期刊论文 前1条

1 张清东,吴越,瞿标,徐俊,安华炜;1220冷连轧机板形控制性能综合改善[J];上海金属;2005年03期

，

本文编号：1659542