合金元素对Mg-Er-Zn-Zr合金铸态组织和力学性能的影响

发布时间：2018-04-06 07:17

  本文选题：Mg-Er-Zn-Zr合金　切入点：显微组织　出处：《铸造技术》2015年12期

【摘要】：研究了合金元素Zn和Zr对Mg-Er-Zn-Zr合金铸态组织和力学性能的影响。结果表明,(Mg_(97.5)Er_2Zn_(0.5))_(99.82)Zr_(0.18)、Mg_(97)Er_2Zn_1和(Mg_(97)Er_2Zn_1)_(99.82)Zr_(0.18)合金都呈现典型的树枝晶结构。由于Zn元素的增加,(Mg_(97)Er_2Zn_1)_(99.82)Zr_(0.18)比(Mg_(97.5)Er_2Zn_(0.5))_(99.82)Zr_(0.18)的组织明显细化,二次枝晶臂的间距减小,第二相由非连续网状分布变成了片层状分布。Zr元素的添加使得合金晶粒细化,第二相呈现更加弥散分布,第二相组成没有发生变化,依然由X-Mg_(12)Er_1Zn_1相和(Mg,Zn)x Er相组成。随着Zn元素和Zr元素含量的增加,合金的力学性能明显提高。
[Abstract]:The effects of Zn and Zr on the microstructure and mechanical properties of Mg-Er-Zn-Zr alloy were studied.The results show that the structure of the typical dendritic structure is observed in the structure of the structure of the structure of the structure of the typical branches in the structure of the structure of the structure of the structure of the branches. The structure of the structure is as follows: (1) the structure of the structure of the branches is typical.The second phase is composed of X-Mg_(12)Er_1Zn_1 phase and Zn-Zn ~ (x) er phase.With the increase of Zn and Zr content, the mechanical properties of the alloy are obviously improved.
【作者单位】： 四川工程职业技术学院材料工程系;枣庄科技职业学院机械工程系;
【分类号】：TG146.22

【相似文献】

相关期刊论文 前10条

1 ;力学性能二级人员取证复习参考题(之一)解答[J];理化检验(物理分册);1997年12期

2 ;力学性能二级人员取证复习参考题(之三)解答[J];理化检验(物理分册);1998年04期

3 陈金宝;高温力学性能二级人员取证复习参考题(持久部分之五)解答[J];理化检验(物理分册);2000年02期

4 潘叶金;电弧熔铸的Nb-18Si-5Mo-5Hf-2C复合材料的力学性能[J];中国钼业;2003年03期

5 张美忠,李贺军,李克智;三维编织复合材料的力学性能研究现状[J];材料工程;2004年02期

6 游宇,周新贵;三维编织复合材料的力学性能[J];纤维复合材料;2004年04期

7 罗文波;唐欣;谭江华;赵荣国;;流变材料长期力学性能加速表征的若干进展[J];材料导报;2007年07期

8 严振宇;徐强;朱时珍;刘颖;;Sm_2Zr_2O_7-ZrB_2/SiC复合材料的制备及力学性能研究[J];稀有金属材料与工程;2011年S1期

9 瞿欣;孙汝n，

本文编号：1718528