退火方式对N36锆合金包壳管性能的影响

发布时间：2018-04-23 08:20

  本文选题：N错合金包壳管 + 退火方式　； 参考：《金属热处理》2015年12期

【摘要】：研究了退火方式对N36错合金包壳管再结晶程度、力学性能、收缩系数(CSR)、椭圆度以及腐蚀性能的影响。结果表明,在同一退火制度下,采用套管与不采用套管退火相比,管材再结晶程度、强度、CSR性能及短期腐蚀性能没有明显差异,伸长率有所下降;采用套管退火的管材椭圆度没有明显变化,而未采用套管进行退火的管材椭圆度增加明显。
[Abstract]:The effects of annealing mode on recrystallization degree, mechanical properties, shrinkage coefficient (CSR), ellipticity and corrosion resistance of N36 alloy cladding tubes were investigated. The results show that there is no significant difference in recrystallization degree, strength and CSR properties and short term corrosion performance between casing and non-casing annealing under the same annealing condition, and the elongation is decreased. The ellipticity of the tube annealed with casing has no obvious change, but the ellipticity of the tube without casing annealing increases obviously.
【作者单位】： 中国核动力研究设计院反应堆燃料及材料国家重点实验室;
【分类号】：TG156.2;TG146.414

【相似文献】

相关期刊论文 前10条

1 王国宏;以气静压法使钛合金粉末致密化用的玻璃包壳[J];稀有金属材料与工程;1983年01期

2 魏晓伟,沈保罗;核反应堆中防护包壳的研究进展[J];稀有金属;2002年04期

3 魏松彦;内表面喷砂处理对锆合金包壳管性能的影响[J];稀有金属材料与工程;1988年04期

4 许咏丽，李军刚，王家英;模拟裂变产物腐蚀对国产不锈钢包壳管室温爆破性能的影响[J];核科学与工程;1995年04期

5 柳祖恩;核电用不锈钢包壳管喷砂处理工艺的得益与局限性[J];上海钢研;1997年02期

6 张莉;徐宏;崔建军;廖礼宝;卢静;;特大型钢包烘烤过程包壳表面温度场研究[J];钢铁;2006年11期

7 许咏丽，王家英，李军刚;国产不锈钢包壳管与裂变产物的化学相互作用──堆外模拟试验[J];核科学与工程;1995年03期

8 张喜燕;;一种关于熔化情况下锆-4合金包壳管氧化物膜厚度变化估计的计算公式[J];渝州大学学报(自然科学版);1989年04期

9 张秀丽;;钛材小容器的密封焊接[J];焊接技术;1986年05期

10 ;化纤纺纱新工艺——ICS包壳纺[J];合成纤维;1979年06期

相关会议论文 前2条

1 陈志强;宋志刚;黄晨;;快堆用316Ti不锈钢包壳管试验研究[A];中国核科学技术进展报告（第二卷）——中国核学会2011年学术年会论文集第4册（核材料分卷、同位素分离分卷、核化学与放射化学分卷）[C];2011年

2 张长义;宁广胜;杨启法;徐远超;佟振峰;林虎;杨文;;M5合金包壳管高温爆破性能[A];中国核学会核材料分会2007年度学术交流会论文集[C];2007年

相关硕士学位论文 前6条

1 周静;国产M5合金组织与性能研究[D];西安工业大学;2010年

2 王倩;130T钢包包壳的温度场和应力场的有限元分析[D];辽宁科技大学;2014年

3 李京;动态应变时效对15-15Ti包壳管拉伸性能影响机制研究[D];安徽大学;2015年

4 张平;吸氢与堆内辐照对Zr-2包壳管拉伸性能影响的研究[D];中国原子能科学研究院;2006年

5 郭琦;超临界水堆包壳候选材料C276高温蠕变特性研究[D];华北电力大学;2012年

6 任丽霞;钠冷快堆系统分析程序实用开发[D];中国原子能科学研究院;2003年

，

本文编号：1791168