2A12铝合金回填式搅拌摩擦点焊接头的组织及性能

发布时间：2018-05-01 02:23

  本文选题：回填式搅拌摩擦点焊 + 微观组织　； 参考：《热加工工艺》2015年23期

【摘要】：试验研究了2A12铝合金回填式搅拌摩擦点焊接头的微观组织及力学性能。结果表明:由于焊接不同区域经历不同的焊接热循环与机械搅拌作用,造成焊接区微观组织的不均匀分布。热影响区组织发生长大并且变暗;热机影响区晶粒被拉长变形,组织不均匀;焊核区发生动态再结晶形成细小等轴晶。焊点的剪切拉伸力学性能较好,达9.193k N,韧性断裂特征明显,韧窝呈抛物线状。
[Abstract]:The microstructure and mechanical properties of 2A12 aluminum alloy backfill friction stir joint were studied. The results show that the microstructure of the welding zone is unevenly distributed due to the different welding heat cycle and mechanical stirring in different welding areas. The microstructure grows and darkens in the heat-affected zone, the grain in the heat-affected zone is elongated and deformed, the microstructure is uneven, and the dynamic recrystallization takes place in the nuke zone to form fine equiaxed crystals. The shear tensile mechanical properties of the solder joints are better, up to 9.193kN. the ductile fracture characteristics are obvious, and the dimples are parabolic.
【作者单位】： 金陵科技学院;福州大学;
【基金】：金陵科技学院科研基金资助项目(40610049)
【分类号】：TG453.9

【参考文献】

相关期刊论文 前1条

1 申志康;杨新岐;张照华;尹玉环;;铝合金回填式搅拌摩擦点焊组织及力学性能分析[J];焊接学报;2013年06期

【共引文献】

相关期刊论文 前8条

1 任俊刚;谢里阳;王磊;郭利鹏;;铝合金回填式搅拌摩擦点焊负载测量分析[J];东北大学学报(自然科学版);2014年09期

2 王希靖;王小龙;张忠科;柴鹏;栾国红;孙学敏;;6082-T6铝合金回填式搅拌摩擦点焊接头的性能[J];兰州理工大学学报;2015年01期

3 王希靖;王小龙;张忠科;栾国红;;铝合金搅拌摩擦点焊疲劳性能研究[J];电焊机;2015年04期

4 林贤军;路浩;;搅拌摩擦点焊疲劳性能研究[J];焊接;2014年10期

5 吴斌涛;苗玉刚;韩端锋;周s，

本文编号：1827321