基于Image J软件的硬质合金显微组织参数化定量分析

发布时间：2018-05-18 20:23

  本文选题：硬质合金 + 显微组织　； 参考：《粉末冶金材料科学与工程》2015年01期

【摘要】：基于体视学原理和硬质合金显微组织特征,结合现代计算机技术,提出一种应用于WC+β(β为粘结相)2相组织的硬质合金显微组织体视学参量定量化表征的方法。利用Image J软件对硬质合金扫描电镜图像进行处理,实现对合金中WC硬质相和粘结相的体积分数、WC晶粒尺寸和分布、WC晶粒形状因子、WC邻接度以及β相平均自由程的参数化定量分析。以WC-8.5Co合金为例,展示合金显微组织参数的定量分析和表征过程。
[Abstract]:Based on the principle of stereology and microstructure characteristics of cemented carbides and modern computer technology, a method for quantifying the stereological parameters of cemented carbides with WC 尾 (尾 as bonded phase) is presented. The scanning electron microscope image of cemented carbide was processed by Image J software. A parameterized quantitative analysis of WC grain size and distribution, WC grain shape factor, WC contiguity and 尾 phase mean free path of WC hard phase and bond phase in the alloy are realized. Taking WC-8.5Co alloy as an example, the quantitative analysis and characterization process of microstructure parameters of the alloy are presented.
【作者单位】： 中南大学粉末冶金国家重点实验室;硬质合金国家重点实验室;
【基金】：硬质合金国家重点实验室开放基金资助项目(201403002) 国家科技重大专项(2012ZX04003-21)
【分类号】：TG135.5

【参考文献】

相关期刊论文 前6条

1 刘国权;;经典体视学的现状、应用及展望[J];材料科学与工程;1992年03期

2 黄志锋,周涛,陈亮;WC晶粒定量测量研究[J];粉末冶金材料科学与工程;2001年03期

3 张立;王元杰;余贤旺;王振波;;WC粉末粒度与形貌对硬质合金中WC晶粒度、晶粒形貌与合金性能的影响[J];中国钨业;2008年04期

4 宋晓艳;赵世贤;刘雪梅;魏崇斌;王海滨;高杨;刘国权;;超细晶硬质合金显微组织与断裂路径的体视学表征研究[J];中国体视学与图像分析;2011年02期

5 张光亮;谢文;黄文亮;黄前葆;陈响明;王社权;;WC粒度分布对WC-Co硬质合金力学性能影响的模拟分析[J];硬质合金;2013年01期

6 张立;王U，

本文编号：1907074