退火温度对Fe-18Mn-3Si-3AlTWIP钢组织和力学性能的影响

发布时间：2018-05-26 18:43

  本文选题：TWIP钢 + 退火温度　； 参考：《热加工工艺》2015年24期

【摘要】：通过金相观察、拉伸试验等方法研究了退火温度对Fe-18Mn-3Si-3AlTWIP钢微观组织、力学性能的影响。结果表明,退火时间相同时,退火温度决定了退火晶粒的尺寸。退火晶粒的尺寸及其均匀性对TWIP钢的力学性能有明显影响。在再结晶温度以上一定范围内退火时,随退火温度的升高,试样钢晶粒尺寸均匀增加,抗拉强度减小,伸长率增加。继续升高温度,晶粒尺寸出现显著差异,抗拉强度和伸长率均降低。
[Abstract]:The effect of annealing temperature on microstructure and mechanical properties of Fe-18Mn-3Si-3AlTWIP steel was studied by metallographic observation and tensile test. The results show that the annealing temperature determines the size of the annealed grain when the annealing time is the same. The size and homogeneity of annealed grains have a significant effect on the mechanical properties of TWIP steel. When the recrystallization temperature is higher than a certain range, the grain size increases uniformly, the tensile strength decreases and the elongation increases with the increase of annealing temperature. When the temperature continues to rise, there is a significant difference in grain size, and the tensile strength and elongation decrease.
【作者单位】： 上海应用技术学院材料科学与工程学院;上海交通大学船舶海洋与建筑工程学院;
【基金】：上海市科委重点支撑项目(13520503100) 国家自然基金项目(51275296)
【分类号】：TG161;TG142.1

【相似文献】

相关期刊论文 前10条

1 王光建;王治;李占峰;汤志伟;;退火温度对FeCoNbVSiBCu合金高频性能的影响[J];河北建筑科技学院学报;2006年03期

2 张晗亮;李增峰;汤慧萍;向长淑;黄愿平;李爱君;;退火温度对铱板材硬度及组织的影响[J];金属热处理;2011年12期

3 郑欣;;退火温度对Al-4.2Cu-1.4Mg合金的微观结构和力学性能的影响[J];金属热处理;2012年11期

4 关学丰;伊春芝;;退火温度对磁盘合金性能的影响[J];湖南冶金;1993年05期

5 贾海龙;张海涛;艾峥嵘;崔建忠;;退火温度对深冷轧制6063铝合金组织性能的影响[J];热加工工艺;2013年22期

6 牟申周;徐国富;王森;尹志民;聂波;蒋蓉蓉;张俊;;退火温度对Al-6Mg-Sc-Zr合金组织与性能的影响[J];中国有色金属学报;2007年11期

7 米振莉;唐荻;代永娟;王海全;;退火温度对25Mn-3Si-3Al-TWIP钢组织和力学性能的影响[J];北京科技大学学报;2007年S2期

8 焦晓亮;吴文博;;不同退火温度和冷却方式对铍青铜组织性能影响的研究[J];宁夏工程技术;2011年04期

9 张帅;李军;曹建春;;退火温度对无取向电工钢组织和磁性能的影响[J];金属热处理;2013年07期

10 王慧芳;退火温度对掺杂钼板性能的影响[J];物理测试;1995年05期

相关会议论文 前10条

1 阳浩;陈德茂;刘奇;辛雪军;吴承汕;;退火温度对微细钨铼合金丝机械性能的影响[A];2009（重庆）中西部第二届有色金属工业发展论坛论文集[C];2009年

2 冯力力;柳q，

本文编号：1938480