高应变速率下Mg-Gd-Y镁合金动态拉伸性能与失效行为

发布时间：2018-06-09 23:00

  本文选题：Mg-Gd-Y镁合金 + 分离式Hopkinson拉杆　； 参考：《沈阳工业大学学报》2015年06期

【摘要】：为了研究Mg-Gd-Y镁合金在高应变速率下的动态拉伸性能及失效机制,采用分离式Hopkinson拉杆(SHTB)装置在室温下且应变速率为1 400~3 000 s-1范围内对其进行了动态拉伸实验,并利用光学显微镜和扫描电子显微镜对动态拉伸后的镁合金试样进行了分析.结果表明,在动态拉伸载荷作用下,Mg-Gd-Y镁合金沿ED方向呈现连续屈服现象.应变速率增大后,Mg-Gd-Y镁合金具有正应变速率效应.在动态拉伸载荷作用下,Mg-Gd-Y镁合金的断口形貌呈解理断裂特征,镁合金的变形方式为孪生和滑移,且滑移为主要变形方式.
[Abstract]:In order to study the dynamic tensile properties and failure mechanism of Mg-Gd-Y magnesium alloy at high strain rate, the dynamic tensile tests were carried out at room temperature with a strain rate of 1 400 ~ 3 000 s ~ (-1) in a split Hopkinson tension bar (SHTB) device. The dynamic tensile magnesium alloy samples were analyzed by optical microscope and scanning electron microscope. The results show that Mg-Gd-Y magnesium alloy exhibits continuous yield along Ed direction under dynamic tensile loading. Mg-Gd-Y magnesium alloy has positive strain rate effect when strain rate increases. The fracture morphology of Mg-Gd-Y magnesium alloy under dynamic tensile loading shows cleavage fracture characteristics. The deformation mode of Mg-Gd-Y magnesium alloy is twinning and slip, and slip is the main deformation mode.
【作者单位】： 沈阳工业大学材料科学与工程学院;
【基金】：国家重点基础研究发展计划(973计划)资助项目(2013CB632205) 辽宁省科技攻关计划资助项目(2013201018)
【分类号】：TG146.22

【相似文献】

相关期刊论文 前3条

1 毛萍莉;于金程;刘正;董阳;席通;;挤压态Mg-Gd-Y镁合金动态压缩力学性能与失效行为[J];中国有色金属学报;2013年04期

2 桑英明;郭永春;李建平;段洪波;;Mg-Gd-Y系合金400℃平衡相图的计算与验证[J];热加工工艺;2012年18期

3 ;[J];;年期

相关博士学位论文 前1条

1 姚素娟;Mg-Gd-Y（Sc）合金的制备技术和高温性能研究[D];中南大学;2009年

相关硕士学位论文 前3条

1 洪敏;Mg-Gd-Y系高强镁合金热机械加工工艺、组织及性能研究[D];沈阳航空航天大学;2015年

2 周阳;表面激冷对Mg-Gd-Y合金的组织、力学和腐蚀性能的影响[D];上海交通大学;2008年

3 梁晓锋;Mg-Gd-Y基高强镁合金组织及性能控制的基础研究[D];重庆理工大学;2012年

，

本文编号：2001121