退火条件对H13钢球化组织与力学性能的影响

发布时间：2018-06-30 05:11

  本文选题：退火 + 碳化物　； 参考：《材料热处理学报》2015年03期

【摘要】：采用扫描电镜观察H13钢不同退火条件退火过程中残留碳化物及退火组织中碳化物形态与分布特征,利用图像处理软件定量分析了碳化物数量、体积分数及大小,并研究了不同退火条件对其相应的回火态力学性能的影响。结果表明,H13钢缓慢冷却退火,选择Ac1~Ac3温度区间短时保温,可获得均匀分布的细小球状残留碳化物,在退火时即使冷却速度较快也可获得球状碳化物均匀分布的退火组织,并保持较好的力学性能。
[Abstract]:The morphology and distribution characteristics of carbides in the residual carbide and annealed microstructure of H13 steel during annealing are observed by scanning electron microscope. The quantity, volume fraction and size of carbides are quantitatively analyzed by image processing software, and the effects of different annealing conditions on the mechanical properties of their corresponding tempering states are studied. The results show that H13 steel is used as a result. The uniform distribution of fine spheroidal residual carbides can be obtained by the slow cooling annealing and short heat preservation in the Ac1~Ac3 temperature range. The uniform distribution of spheroidal carbides can be obtained, and the better mechanical properties are maintained even if the cooling rate is faster in annealing.
【作者单位】： 北京科技大学新材料技术研究院;北京科技大学新金属材料国家重点实验室;
【分类号】：TG156.2;TG142.1

【参考文献】

相关期刊论文 前10条

1 惠卫军,于同仁,苏世怀,董瀚,翁宇庆;中碳钢球化退火行为和力学性能的研究[J];钢铁;2005年09期

2 刘宗昌,李文学,孙立新,邵淑艳;H13等工模具钢退火软化新工艺[J];国外金属热处理;2000年01期

3 崔];中国模具钢现状及发展(Ⅰ)[J];机械工程材料;2001年01期

4 胡明,韩季平;残留碳化物在等温球化处理中的作用[J];佳木斯工学院学报;1994年03期

5 邹安全,邓芬燕,邓沛然;等温球化退火对H13钢组织和性能的影响[J];金属热处理;2003年08期

6 陆明和;田玉新;蔡海燕;殷光虹;;高温均匀化退火对H13钢芯棒带状偏析和冲击性能的影响[J];金属热处理;2010年08期

7 周健;马党参;张才明;康爱军;李向阳;陈再枝;;不同退火工艺对H13钢组织和力学性能的影响[J];金属热处理;2012年05期

8 王明;马党参;刘振天;周健;迟宏宵;代建清;;Nb对芯棒用H13钢偏析、液析碳化物及力学性能的影响[J];金属学报;2014年03期

9 章为夷;球化处理中残留碳化物的作用[J];热加工工艺;1992年04期

10 任慧平，李文学，，刘宗昌，王玉峰;H13钢软化退火工艺的研究[J];热加工工艺;1996年06期

【共引文献】

相关期刊论文 前10条

1 刘涛;杨王s

本文编号：2085046