IN690高温合金管材挤压变形动态再结晶模拟

发布时间：2018-06-30 05:49

  本文选题：IN + 高温合金　； 参考：《材料热处理学报》2015年S2期

【摘要】：对IN690高温合金管材挤压变形过程中的动态再结晶进行了模拟研究,获得了不同挤压工艺条件下动态再结晶与平均晶粒尺寸的变化规律。研究表明:在挤压速度和挤压比一定的条件下,随着挤压温度的升高,完全动态再结晶区域变大,平均晶粒尺寸增大;在挤压速度和挤压温度一定的条件下,随着挤压比的增大,完全动态再结晶区域变大,平均晶粒尺寸减小;管材壁厚方向上由内壁向外平均晶粒尺寸呈现先增大后减小的规律;平均晶粒尺寸的模拟值与实验值的相对误差小于12%。
[Abstract]:The dynamic recrystallization of IN690 high - temperature alloy tubes during extrusion deformation is simulated . The changing law of dynamic recrystallization and average grain size under different extrusion conditions is obtained . The results show that , with the increase of extrusion temperature , the average grain size increases with the increase of extrusion temperature . The average grain size decreases with the increase of extrusion ratio . The average grain size of the tube wall is increased first and then decreases with the increase of extrusion ratio . The relative error of the average grain size and the experimental value is less than 12 % .
【作者单位】： 沈阳理工大学材料科学与工程学院;
【基金】：国家自然科学基金重点项目(51575366)
【分类号】：TG376

【相似文献】

相关期刊论文 前10条

1 邓小虎;张立文;何燕;裴继斌;卢愈;;应变速率对金属动态再结晶影响的数值模拟[J];塑性工程学报;2007年02期

2 邓小虎;张立文;卢瑜;裴继斌;;动态再结晶过程的三维元胞自动机模拟[J];金属热处理;2009年04期

3 谢章龙;刘振宇;王国栋;;低碳9Ni钢的动态再结晶数学模型[J];东北大学学报(自然科学版);2010年01期

4 王丽君;关小军;禹宝军;赵健;;热加工材料动态再结晶介观组织模拟模型的研究进展[J];山东大学学报(工学版);2010年03期

5 王琴;方绿频;;动态再结晶过程的定量化可视化元胞自动机模拟[J];机械工程学报;2011年22期

6 麻晓飞;;动态再结晶过程的元胞自动机模拟[J];热加工工艺;2012年02期

7 金泉林;一个新的动态再结晶过程的分析模型[J];塑性工程学报;1994年01期

8 何宜柱，雷廷权，高甲生，陈大宏;动态再结晶细化模型[J];华东冶金学院学报;1995年02期

9 何宜柱，陈大宏，雷廷权，，黄丽萍;动态再结晶动力学模型的研究[J];华东冶金学院学报;1995年02期

10 杜随更,吴诗,段立宇,程功善;初始动态再结晶过程中的位错动态行为[J];西北工业大学学报;1997年03期

相关会议论文 前10条

1 何燕;张立文;牛静;;利用元胞自动机方法模拟多晶金属材料的动态再结晶过程[A];2004年中国材料研讨会论文摘要集[C];2004年

2 史志远;马长文;;35K钢的动态再结晶模型研究[A];2007中国钢铁年会论文集[C];2007年

3 曲杰;金泉林;;伴随动态再结晶的黏塑性本构关系的材料参数识别[A];2002年材料科学与工程新进展（下）——2002年中国材料研讨会论文集[C];2002年

4 张羊换;;微合金化钢的动态再结晶及沉淀强化的研究[A];第八届全国塑性加工理论与新技术学术会议论文集[C];1999年

5 李龙飞;杨王s

本文编号：2085182