亚共析铀铌合金激光焊接微观结构及电化学行为

发布时间：2018-07-05 19:32

  本文选题：亚共析铀铌合金 + 激光焊接　； 参考：《稀有金属材料与工程》2015年02期

【摘要】：采用光学显微镜、扫描电镜、X射线衍射仪和电化学综合测试仪对亚共析珠光体铀铌合金激光焊接接头的微观结构和电化学行为开展了研究,结果显示:亚共析珠光体铀铌合金焊缝晶粒尺寸约50μm,焊缝相结构为单相正交结构α`马氏体;在50μg/g Cl-的Na Cl溶液中,焊缝金属腐蚀电位比基材低约400 m V,构成了电偶腐蚀对,在电偶腐蚀和自腐蚀共同作用下,焊接接头的腐蚀电流比焊缝金属和基材分别高约3至10倍,接头整体抗腐蚀性能低于基材,腐蚀形式表现为均匀腐蚀。
[Abstract]:The microstructure and electrochemical behavior of the subeutectoid pearlite uranium niobium alloy laser welded joint were studied by optical microscope, scanning electron microscope, X ray diffractometer and electrochemical synthetic tester. The results showed that the grain size of the subeutectoid perlite uranium niobium alloy weld grain size was about 50 u m, and the weld phase structure was a single-phase orthogonal structure of the alpha martensite. In the Na Cl solution of 50 g/g Cl-, the corrosion potential of the weld metal is about 400 m V lower than that of the substrate, and the galvanic corrosion is formed. The corrosion current of the welded joint is about 3 to 10 times higher than that of the weld metal and the base material under the combination of galvanic corrosion and self corrosion. The corrosion resistance of the joint can be lower than the base material and the corrosion form is uniform corrosion.
【作者单位】： 中国工程物理研究院;
【基金】：中国工程物理研究院发展基金支持
【分类号】：TG456.7

【相似文献】

相关期刊论文 前10条

1 王小英;郎定木;杨建雄;姜桂芬;;低应变率下形变对亚共析U-Nb合金微观组织结构的影响[J];材料导报;2007年S3期

2 周志宏;徐祖耀;许龙元;;亚共析掽中魏氏}D~T的长大速率[J];上海交通大学学报;1964年01期

3 申亮,张鹏程,陈向林,唐县娥;一种铸态亚共析U-Nb合金晶粒细化的热处理工艺研究[J];稀有金属材料与工程;2004年10期

4 ;[J];;年期

5 ;[J];;年期

6 ;[J];;年期

7 ;[J];;年期

8 ;[J];;年期

9 ;[J];;年期

10 ;[J];;年期

，

本文编号：2101489