三价铈离子对制冷设备用铝管表面有机-无机杂化膜耐蚀性能的影响（英文）

发布时间：2018-08-20 14:51

【摘要】：采用溶胶-凝胶法在制冷设备用铝管表面制备三价铈离子作为添加剂的有机-无机杂化膜,通过傅里叶变换红外光谱确认其结构。性能测试结果表明:当三价铈离子浓度达到1.5 mmol/L时,所得到的杂化膜的耐蚀性能有明显的改善;与空白试样相比,其中CuSO_4的变色时间延长到500s,耐酸和耐碱腐蚀速率分别降低了67%和70%,盐雾试验结果也表现出很好的耐蚀性。电化学测试表明,杂化膜试样的自腐蚀电流密度和自腐蚀电压分别为2.877×10~(-7)A/cm~2和-0.550 V。金相和扫描电镜图片显示杂化膜均匀致密。X射线能谱分析表明该膜层主要由Al、Si和Ce等元素组成。
[Abstract]:The organic-inorganic hybrid film with cerium trivalent as additive was prepared on the surface of aluminum tube by sol-gel method. The structure of the film was confirmed by Fourier transform infrared spectroscopy (FTIR). The results show that the corrosion resistance of the hybrid film is improved obviously when the concentration of cerium ion reaches 1.5 mmol/L, and the corrosion resistance of the hybrid film is better than that of the blank sample. When the discoloration time of CuSO_4 was prolonged to 500s, the corrosion rates of acid and alkali resistance were decreased by 67% and 70%, respectively. The salt spray test results also showed good corrosion resistance. The electrochemical measurements show that the self-corrosion current density and the self-corrosion voltage of the hybrid films are 2.877 脳 10 ~ (-7) A/cm~2 and -0.550 V, respectively. Metallographic and SEM images show that the hybrid film is homogeneous and compact. X-ray energy dispersive analysis shows that the film is mainly composed of Al Si and ce elements.
【作者单位】： 长江大学化学与环境工程学院;中南大学化学化工学院;
【基金】：Project(51404038)supported by the National Natural Science Foundation of China
【分类号】：TG174.4;TB657

【参考文献】

相关期刊论文 前3条

1 肖围;满瑞林;缪畅;彭天兰;;Study on corrosion resistance of the BTESPT silane cooperating with rare earth cerium on the surface of aluminum-tube[J];Journal of Rare Earths;2010年01期

2 Ojo Sunday Isaac FAYOMI;Abimbola Patricia Idowu POPOOLA;;四元复合薄膜的形成特征、摩擦特性和耐腐蚀性能(英文)[J];Transactions of Nonferrous Metals Society of China;2014年10期

3 D.SEIFZADEH;A.BEZAATPOUR;R.ASADPOUR JOGHANI;;酸性介质中N,N′-双(2-亚甲基吡啶)-1,2-亚氨基乙烷对AZ91D镁合金的腐蚀抑制作用(英文)[J];Transactions of Nonferrous Metals Society of China;2014年11期

【共引文献】

相关期刊论文 前5条

1 梁永煌;满瑞林;;Al管表面有机杂化膜的制备及性能表征[J];金属学报;2010年12期

2 周洋;鲁道荣;;镀锌钢表面硅烷膜的耐蚀性能研究[J];金属功能材料;2012年06期

3 肖围;李新海;郭华军;王志兴;杨波;吴贤文;;Preparation and properties of composite polymer electrolyte modified with nano-size rare earth oxide[J];Journal of Central South University;2012年12期

4 肖围;李新海;王志兴;郭华军;王接喜;黄思林;甘雷;;Physicochemical properties of a novel composite polymer electrolyte doped with vinyltrimethoxylsilane-modified nano-La_2O_3[J];Journal of Rare Earths;2012年10期

5 史菲;王春青;张忠明;;铸态Mg-Zn-Y-(Gd)合金凝固组织、腐蚀性能和力学性能（英文）[J];Transactions of Nonferrous Metals Society of China;2015年07期

相关博士学位论文 前1条

1 王雷;镀锌板表面硅烷复合钝化膜的制备、性能和成膜机理[D];东北大学;2012年

【二级参考文献】

相关期刊论文 前7条

1 顾宝珊;刘建华;;Corrosion Inhibition Mechanism of Rare Earth Metal on LC4 Al Alloy with Spilt Cell Technique[J];Journal of Rare Earths;2006年01期

2 徐瑞东;王军丽;郭忠诚;王华;;Effects of rare earth on microstructures and properties of Ni-W-P-CeO_2-SiO_2 nano-composite coatings[J];Journal of Rare Earths;2008年04期

3 彭天兰;满瑞林;;Rare earth and silane as chromate replacers for corrosion protection on galvanized steel[J];Journal of Rare Earths;2009年01期

4 伍立坪;赵京京;谢永平;杨中东;;Progress of electroplating and electroless plating on magnesium alloy[J];Transactions of Nonferrous Metals Society of China;2010年S2期

5 J.SUDAGAR;连建设;陈晓明;朗鹏;梁亚琴;;无铬转化膜预处理提高AZ91D镁合金化学镀Ni-P的腐蚀性能(英文)[J];Transactions of Nonferrous Metals Society of China;2011年04期

6 朱旭蓓;蔡超;郑国渠;张昭;李劲风;;纳米结构Ni-TiN复合薄膜的电沉积及腐蚀行为(英文)[J];Transactions of Nonferrous Metals Society of China;2011年10期

7 杨广彬;柴单淘;熊秀娟;张晟卯;余来贵;张平余;;表面修饰Cu纳米微粒的制备及摩擦学性能(英文)[J];Transactions of Nonferrous Metals Society of China;2012年02期

【相似文献】

相关期刊论文 前10条

1 宋霖;韦奇;郝润秋;聂祚仁;李群艳;;十七氟癸基修饰的有机-无机杂化二氧化硅膜材料的制备及气体分离性能[J];高等学校化学学报;2012年08期

2 ;专利:有机-无机杂化涂料[J];有机硅氟资讯;2005年07期

3 王乾;安瑛;谢鹏程;杨卫民;丁玉梅;;有机-无机杂化复合材料膜内层叠制备新方法[J];现代塑料加工应用;2011年05期

4 刘丰yN,符连社,王俊,张洪杰;有机-无机杂化中孔材料研究进展[J];化学通报;2002年10期

5 王秀华;孙红霞;刘守华;;硅溶胶改性有机-无机杂化纳米薄膜的制备及性能测试[J];腐蚀与防护;2008年01期

6 李胜利;杨捷;郁建华;吴杰颖;田玉鹏;;新型有机-无机杂化吡啶盐化合物的设计合成[J];安徽大学学报(自然科学版);2009年04期

7 刘长军;田丰;陈世谦;张彦军;刘圣军;;有机-无机杂化纳米结构体——多面体低聚硅倍半氧烷研究进展[J];中国塑料;2005年09期

8 蒋芸;吴晓建;李艺;杨永刚;李宝宗;;自组织多孔海绵状有机-无机杂化二氧化硅[J];分子科学学报;2009年03期

9 张敏;田晶;张瑾;李凌智;柳清菊;;有机-无机杂化介孔薄膜的研究进展[J];材料导报;2009年S1期

10 赵飞燕;高艳阳;;层状有机/无机杂化物(C_4H_9NH_3)_2NiCl_4的合成与表征(英文)[J];化学研究;2014年01期

相关会议论文 前10条

1 陈海龙;杨扬;王义展;李昊龙;吴立新;;新型热敏有机-无机杂化树枝状复合物的合成与表征[A];中国化学会第十三届胶体与界面化学会议论文摘要集[C];2011年

2 方章建;王世敏;董兵海;杨琼峰;;含咔唑类有机-无机杂化功能材料的制及其性能研究[A];中国化学会第二十五届学术年会论文摘要集（下册）[C];2006年

3 于旭彪;韦朝海;胡芸;吴超飞;;新型有机-无机杂化蛭石吸附材料的制备与应用[A];第六届全国环境化学大会暨环境科学仪器与分析仪器展览会摘要集[C];2011年

4 林旭平;张国昌;马景陶;张宝清;;聚倍半硅氧烷有机-无机杂化氢气分离膜的制备与性能[A];全国第三届溶胶—凝胶科学技术学术会议论文摘要集[C];2004年

5 王世敏;游婷;许祖勋;;有机-无机杂化薄膜的制备及热释电性能研究[A];中国化学会第26届学术年会有机固体材料分会场论文集[C];2008年

6 吴立新;;有机-无机杂化反胶束的溶液聚集与结构[A];中国化学会第十二届胶体与界面化学会议论文摘要集[C];2009年

7 汪理文;李艺;李宝宗;杨永刚;;手性有机-无机杂化二氧化硅结构的形成[A];中国化学会第三届全国分子手性学术研讨会论文集[C];2010年

8 于伟;王永亮;韩耀坤;胡敏标;王维;;主链中含有杂多酸的新型聚酰胺类有机-无机杂化聚合物的合成与表征[A];2010年全国高分子材料科学与工程研讨会学术论文集（上册）[C];2010年

9 魏永怀;张婷;颜力楷;苏忠民;;具有不同π-共轭桥结构的多酸基有机-无机杂化染料敏化剂的理论设计[A];第六届全国物理无机化学会议论文摘要集[C];2012年

10 石玉元;张印;刘晶晶;周哲;孙宾;俞昊;朱美芳;;有机-无机杂化低维材料结构设计与功能调控[A];2009年全国高分子学术论文报告会论文摘要集（下册）[C];2009年

相关硕士学位论文 前10条

1 宋霖;十七氟癸基修饰的有机-无机杂化二氧化硅膜材料及氢气分离研究[D];北京工业大学;2012年

2 周爱民;功能性有机-无机杂化多金属氧酸盐研究[D];安徽大学;2002年

3 张信信;新型功能有机—无机杂化离子通道膜的制备与表征[D];北京林业大学;2012年

4 游小燕;过渡金属硼氧、磷氧杂化化合物的制备、结构及表征[D];西安电子科技大学;2010年

5 罗淼;叠氮有机—无机杂化硅胶的制备与应用[D];华东理工大学;2011年

6 刘坤;基于多金属钨酸盐的有机-无机杂化化合物的水热合成及性质研究[D];东北师范大学;2006年

7 武淑军;不同维度的有机—无机杂化钒酸盐的合成、结构与性能[D];北京理工大学;2015年

8 陈延辉;钒簇有机—无机杂化化合物的水热合成和结构表征[D];东北师范大学;2004年

9 史振雨;基于多金属氧簇建筑块的有机-无机杂化化合物的分子设计、水热合成和结构表征[D];东北师范大学;2006年

10 王凤鹭;有机—无机杂化二氧化钛光催化材料的制备及性能研究[D];东北林业大学;2011年

，

本文编号：2194032