两种纤维桩短期修复效果的临床观察

发布时间：2018-04-16 02:23

本文选题：纤维桩 + 牙体缺损　；参考：《华西口腔医学杂志》2014年04期

【摘要】：目的观察两种玻璃纤维桩修复系统修复牙齿缺损的短期临床疗效。方法选择北京宣武中医医院口腔科门诊和北京大学口腔医院特诊科因牙体缺损进行桩核冠修复的符合纳入标准的120例患者,经知情同意后,随机分2组,每组60例,分别采用Tenax Fiber White纤维桩与国产OUYA FIBER纤维桩修复系统修复,修复后1周与3个月复诊,检查纤维桩修复的临床效果。结果 Tenax Fiber White纤维桩与OUYA FIBER纤维桩修复1周后,检查纤维桩修复体的总体情况、边缘密合性、边缘着色情况,两组满意率均达到98%以上;3个月后复查,通过X线片检查纤维桩的总体情况和基牙情况,以及咀嚼功能恢复情况,两组满意率均达到96%以上;2组间比较差异无统计学意义(P0.05)。结论 OUYA FIBER纤维桩与Tenax Fiber White纤维桩在3个月的观察期间的总体疗效相当,值得推广应用,但仍需对其疗效进行长期的临床观察。
[Abstract]:Objective to observe the short-term clinical effect of two kinds of glass fiber post repair system for repairing tooth defect.Methods one hundred and twenty patients with dental defects in Beijing Xuanwu Hospital of traditional Chinese Medicine and Department of Stomatology of Peking University were selected. After informed consent, 120 patients were randomly divided into 2 groups, 60 cases in each group.The Tenax Fiber White fiber post and the domestic OUYA FIBER fiber pile were used to repair the patients respectively. The clinical effect of the repair was examined at 1 week and 3 months after the repair.Results after the restoration of Tenax Fiber White fiber pile and OUYA FIBER fiber pile for 1 week, the overall condition, edge compactness, edge coloration of the two groups were examined, and the satisfaction rate of the two groups was over 98%.The overall condition of fiber pile and abutment and the recovery of masticatory function were examined by X-ray film. The satisfaction rate of the two groups was above 96% and there was no significant difference between the two groups (P 0.05).Conclusion the total curative effect of OUYA FIBER fiber pile and Tenax Fiber White fiber pile is equal to that of Tenax Fiber White fiber pile in 3 months. It is worth popularizing and applying, but it is still necessary to make long-term clinical observation on the effect of OUYA FIBER fiber pile and Tenax Fiber White fiber pile.
【作者单位】：北京市宣武中医医院口腔科;北京大学口腔医院特诊科;
【基金】：国家“十二五”科技支撑计划基金资助项目(2012BAI-07B00) 中央保健科研课题基金资助项目(W2013BJ41)
【分类号】：R783.1

【共引文献】