发布时间：2018-09-11 19:45

【摘要】：目的比较铅橡胶射线防护品在不同被覆材料及不同缝合方式时的铅防渗效果。方法测定4个时间点的8个琼脂块载体样本点的铅含量,共测5次,经数据有效性处理后,计算两种射线防护制品的表面及边缘的铅渗出量及铅渗出比率。结果两种样品表面及边缘在0.5、1、3、5 h 4个时间点每组铅渗出量差异均无统计学意义(P0.05)。样品表面及边缘的铅渗出量及铅渗出比率尼龙TPU复合布周边热合加工的防护品均明显低于尼龙布周边缝合的防护品;两种样品的铅渗出量边缘均比表面要高,差异均有统计学意义(P0.01)。尼龙TPU复合布周边热合加工的防护品表面及边缘铅渗出比率数值数量级分别为10-5和10-4;尼龙布周边缝合防护品分别为10-3和10-1。结论双层封闭的尼龙TPU复合布周边热合加工的铅橡胶防护品比尼龙布周边缝合的防护品显著减少铅渗出。
[Abstract]:Objective To compare the anti-seepage effect of lead rubber protective products with different coating materials and different suture methods.Methods Lead content in 8 samples of agar block carrier at 4 time points was measured for 5 times.After data validity treatment,the lead leakage and lead leakage ratio on the surface and edge of two protective products were calculated. There was no significant difference in lead leakage between the two groups at 0.5, 1, 3, and 5 h (P 0.05). The surface and edge lead exudation ratios were 10-5 and 10-4, respectively, and 10-3 and 10-1, respectively. Conclusion The lead rubber protective products of double-layer closed nylon TPU composite fabric were better than that of nylon TPU composite fabric. Cloth around stitched protective products significantly reduced lead exudation.
【作者单位】： 青岛大学医学院附属烟台毓璜顶医院医学影像科;青岛大学医学院;山东省烟台市莱山区第一人民医院放射科;青岛大学医学院附属医院PET-CT中心;
【分类号】：R143

【相似文献】

相关期刊论文 前10条

1 董海斌,张丹枫,历凤云;国产与进口铅橡胶制品防护性能比较[J];中国航天工业医药;2000年03期

2 孟斌，张丹枫，冯涛，赵兰才，朱建国;我国铅橡胶类防护用品的防护性能及评价[J];中华放射医学与防护杂志;1994年02期

3 林志凯,赵兰才,金辉,崔广志,葛淑清;国产铅橡胶板的物理性能和防护质量及评价[J];中国辐射卫生;1997年02期

4 ;[J];;年期

5 ;[J];;年期

6 ;[J];;年期

7 ;[J];;年期

8 ;[J];;年期

9 ;[J];;年期

10 ;[J];;年期

相关会议论文 前1条

1 王宗成;魏士栋;祁吉;;卧式性腺X线防护器[A];全国医用辐射防护与安全学术研讨会论文汇编[C];2004年

相关重要报纸文章 前1条

1 孟晶;无铅新材料有望取代传统铅橡胶[N];中国化工报;2006年

，

本文编号：2237688