【摘要】：在组织工程支架表面沉积含有生长因子的丝蛋白层,通过丝蛋白β构象转变,固定生长因子于支架表面。研究此种生长因子负载方法对明胶多孔支架性能的影响,结果表明,因子负载前后支架的孔隙率皆达到90%以上,吸水量皆为干燥时支架质量的18倍左右;力学测试表明,因子负载后支架的压缩模量增加至26.1kPa;Elisa检测表明,在各取样时间点,每毫克支架缓释活性EGF的量约在0.3~0.5ng之间,4周累积释放活性EGF达到3.473ng;MTT实验与SEM观察表明,用此种方法负载因子于支架中,可以有效促进支架中细胞的生长。
[Abstract]:The silk protein layer containing the growth factor is deposited on the surface of the tissue engineering scaffold, and the growth factor is fixed on the surface of the support through the conformational change of the silk protein. The effect of the loading method of the growth factor on the performance of the gelatin porous scaffold was studied. The results showed that the porosity of the support before and after the loading of the factor was over 90%, and the amount of water absorption was about 18 times the mass of the support at the time of drying; the mechanical tests showed that, The compressive modulus of the support after the factor loading was increased to 26.1 kPa; the Elisa test showed that, at each sampling time point, the amount of the sustained-release active EGF per mg of the stent was about 0.3 to 0.5 ng, and the cumulative release activity of EGF at 4 weeks reached 3.473 ng; and the MTT assay and the SEM observation showed that the loading factor of this method was in the stent, The growth of cells in the stent can be effectively promoted.
【作者单位】： 广州医科大学基础学院生物医学工程系;
【基金】：国家自然科学基金资助项目(50872099) 广东省重大科技专项基金资助项目(2012A080203002) 广州医科大学博士人员科研资助项目(2012C17)
【分类号】：R318.08

【共引文献】

相关期刊论文 前10条

1 王芋骁;孔志杰;黄溪;马林;;交联改性丝素蛋白材料制备和医学应用[J];现代丝绸科学与技术;2013年05期

2 黄君霆;;家蚕基因组序列解读10周年[J];蚕业科学;2013年05期

3 胡戈亮;马永刚;姚遥;王善文;;明胶-白芨胶/丹参多孔材料与大鼠组织相容性研究[J];湖北中医药大学学报;2013年06期

4 ZHANG LuZhong;ZHOU YouLang;LI GuiCai;ZHAO YaHong;GU XiaoSong;YANG YuMin;;Nanoparticle mediated controlled delivery of dual growth factors[J];Science China(Life Sciences);2014年02期

5 朱继翔;陈晓明;彭晔;阳范文;田秀梅;何福坡;;负载丝裂霉素C的明胶多孔支架制备及释放[J];合成材料老化与应用;2014年02期

6 辛林伟;唐际存;李朝旭;李强;王黎明;;不同途径注射鼠神经生长因子对断指再植术后感觉恢复的疗效评估[J];实用医学杂志;2013年19期

7 Huawei Liu;Weisheng Wen;Min Hu;Wenting Bi;Lijie Chen;Sanxia Liu;Peng Chen;Xinying Tan;;Chitosan conduits combined with nerve growth factor microspheres repair facial nerve defects[J];Neural Regeneration Research;2013年33期

8 LIU Bingjie;WANG Dongfeng;YU Guangli;MENG Xianghong;;Adsorption of Heavy Metal Ions,Dyes and Proteins by Chitosan Composites and Derivatives-A Review[J];Journal of Ocean University of China;2013年03期

9 陈格飞;贾小娜;郑翔宇;孟清;;重组蜘蛛丝蛋白MiSp NT结构域在不同pH环境下的Trp荧光光谱及圆二色谱分析[J];中国生物化学与分子生物学报;2014年01期

10 金洹宇;刘星;银华;安艳;;丝素蛋白在生物医用领域中的应用[J];生物医学工程学杂志;2014年01期

相关会议论文 前1条

1 苏欢欢;孙华燕;高旭鹏;王鑫;徐风华;;脑源性神经营养因子复合导管对大鼠坐骨神经损伤修复的研究[A];2013年中国药学大会暨第十三届中国药师周论文集[C];2013年

相关博士学位论文 前2条

1 王宇清;PFTBA水凝胶促进周围神经再生的效能及机制研究[D];第四军医大学;2013年

2 杨小元;丝涤混构小口径人造血管的成型及性能研究[D];东华大学;2014年

相关硕士学位论文 前10条

1 向杰;可吸收诱导神经修复材料用于周围神经缺损的实验研究及初步临床应用[D];南方医科大学;2012年

2 王宁;木材/羟基磷灰石骨替代复合材料的制备及研究[D];安徽大学;2013年

3 张海卫;雷帕霉素、FK506对大鼠雪旺细胞增殖、迁移及相关蛋白表达影响的对比研究[D];南华大学;2013年

4 李阳;壳聚糖复合膜上及移植部位黑素细胞的实验研究[D];安徽医科大学;2013年

5 赵鹏程;低强度超声对iPSCs源性神经嵴干细胞增殖和分化的影响[D];重庆大学;2013年

6 曾佳佳;赤泥改性及其与壳聚糖复合吸附Cr（Ⅵ）的研究[D];广西大学;2013年

7 胡辉;新型神经导管复合材料与骨髓间充质干细胞用于周围神经缺损的基础研究[D];南方医科大学;2013年

8 张敏;丙氨瑞林PLGA微球缓释给药系统的研究[D];第二军医大学;2013年

9 马骁;静电纺丝制备PLGA三维组织工程支架的研究[D];大连医科大学;2013年

10 苏欢欢;脑源性神经营养因子复合导管对大鼠坐骨神经损伤修复的影响[D];河北北方学院;2013年

【相似文献】

相关期刊论文 前10条

1 李U，

本文编号：2452745