镁合金支架植入兔腹主动脉后降解时间及血管内膜增生观察

发布时间：2018-06-22 15:54

  本文选题：可降解镁合金支架 + 腹主动脉　； 参考：《介入放射学杂志》2017年05期

【摘要】：目的观察新型可降解镁合金支架——MPM植入兔腹主动脉后降解时间及血管内膜增生。方法 24只新西兰大白兔随机分为4组,每组6只,分别于距左肾动脉水平下1 cm腹主动脉处植入MPM支架各1枚。术后30、60、90、180 d分别复查腹主动脉造影,分离支架段血管进行观察。采用SPSS20.0软件对数据进行分析。结果 24只实验兔在随访期间存活良好。植入支架逐渐降解,180 d时基本降解;血管内膜增生,90 d时达峰值,整个降解过程血管通畅。结论可降解镁合金支架MPM完全降解时间为182 d,可满足血管正性重塑。
[Abstract]:Objective to observe the degradation time and intimal hyperplasia of new degradable magnesium alloy scaffolds (MPM) implanted into rabbit abdominal aorta. Methods Twenty-four New Zealand white rabbits were randomly divided into 4 groups with 6 rabbits in each group. MPM stents were implanted at the abdominal aorta 1 cm below the left renal artery level in each group. Abdominal aortography was performed 30 days after operation and stent segments were separated for observation. SPSS 20.0 software was used to analyze the data. Results 24 rabbits survived well during follow-up. The stents degraded basically at 180 d and reached the peak at 90 d after intimal hyperplasia. The whole degradation process was smooth. Conclusion MPM degradation time of degradable magnesium alloy scaffold is 182 d, which can satisfy positive vascular remodeling.
【作者单位】： 上海交通大学附属第六人民医院南院介入科;浙江省嘉兴市第一医院放射科;
【基金】：上海市科委医学引导类项目(124119b1200) 上海市卫生局科研项目(20124175)
【分类号】：R654.3

【相似文献】

相关期刊论文 前8条

1 余汇洋;;损伤血管内膜增生的研究[J];局解手术学杂志;2006年03期

2 王民生,陈中伟;生长因子与血管内膜增生[J];中华创伤杂志;1994年05期

3 李济宇;血管内膜增生的治疗进展[J];国外医学.外科学分册;1998年04期

4 钱济先,钱兆奇,黄耀添,李桂云,王剑波,胡佩珍,王军,吕荣;含β射线的软性血管外模型对移植血管内膜增生及平滑肌增殖的抑制作用[J];中华医学杂志;1999年01期

5 曲乐丰;反义技术治疗血管内膜增生的研究[J];国外医学(创伤与外科基本问题分册);2000年01期

6 裴斐;李俊彦;张莉;何蕊;;内皮型一氧化氮合酶基因转染对移植人工血管内膜增生的作用(英文)[J];中国组织工程研究与临床康复;2008年40期

7 李超,李桂媛,张强,段志泉;一氧化氮对人培养血管内膜增生的抑制作用[J];中华实验外科杂志;2000年03期

8 ;[J];;年期

相关硕士学位论文 前1条

1 巢雄杰;金粉蕨素对大鼠颈动脉损伤后狭窄的早期预防作用的研究[D];南华大学;2016年

，

本文编号：2053345