低合金耐蚀钢筋在两种pH混凝土模拟孔溶液中的耐氯离子点蚀性能

发布时间：2018-01-08 17:41

本文关键词：低合金耐蚀钢筋在两种pH混凝土模拟孔溶液中的耐氯离子点蚀性能　出处：《东南大学学报(自然科学版)》2015年06期 　论文类型：期刊论文

【摘要】：对比研究了普通低碳钢筋(LC)和2种耐蚀钢筋(1%Cr和6%Cr)在未碳化(p H=12.6)与碳化(p H=10.6)模拟混凝土孔溶液中加入氯离子后的腐蚀行为.采用线性极化电阻(LPR)和电化学阻抗谱(EIS)表征钢筋的电化学行为,并通过扫描电子显微镜(SEM)和X射线能谱仪(EDS)对腐蚀产物进行微观形貌观察和元素分析.结果表明:在点蚀阶段,与LC钢筋相比,1%Cr钢筋的临界氯离子值未提高,而6%Cr钢筋则提高5~10倍;在腐蚀扩展阶段,1%Cr的耐蚀性能与LC钢筋相比有小幅提升,可能的原因是1%Cr钢筋中的Cr促使生成致密锈层.
[Abstract]:Comparative study of ordinary low carbon steel (LC) and 2 kinds of corrosion resistant steel (1%Cr and 6%Cr) in (P H=12.6) and carbide carbide (P H=10.6) added after the chloride ion corrosion behavior in simulated concrete pore solution. The linear polarization resistance (LPR) and electrochemical impedance spectroscopy (EIS) surface electrochemical behavior syndrome bar, and by scanning electron microscopy (SEM) and X ray spectrometer (EDS) analysis and microstructure observation of elements on corrosion products. The results showed that: in the pitting stage, compared with LC steel, 1%Cr Steel's critical chloride value is not increased, and the 6%Cr steel bars is increased by 5~10 times during the extension period; 1%Cr corrosion, corrosion resistance and LC steel compared to a slight increase, the possible reason is that 1%Cr reinforced Cr in promoting the formation of dense rust layer.

【作者单位】：东南大学江苏省土木工程材料高技术研究重点实验室;
【基金】：国家自然科学基金资助项目(51278098;51208098) 江苏省重点科技成果转化专项基金资助项目(85120000220)
【分类号】：TU528.571;TG142.1
【正文快照】： 目前在各种建筑工程中广泛采用钢筋混凝土结构.由氯离子入侵和混凝土碳化等因素引起的钢筋腐蚀问题日益严重.钢筋腐蚀产物体积膨胀将导致混凝土结构开裂,引起混凝土结构的过早破坏,给当今世界各国造成了严重的经济损失[1-2].采用耐蚀性相对较好且力学性能优异的合金耐蚀钢筋代