  本文关键词： 轻骨料混凝土 钢纤维 早期变形 抗裂性 强度　出处：《公路工程》2016年05期 　论文类型：期刊论文

【摘要】：为研究钢纤维轻骨料混凝土的早期变形和抗裂能力,通过室内试验对不同掺量的钢纤维粉煤灰轻骨料混凝土进行早期体积收缩变形和抗裂试验,试验结果表明:在粉煤灰轻骨料混凝土中掺入钢纤维可有效抑制混凝土的收缩,随着钢纤维掺量的增加,减缩效果越来越显著;掺入钢纤维后,粉煤灰轻骨料混凝土的抗压强度和劈裂抗拉强度均得到一定程度的提高,且随钢纤维掺量的增加呈上升趋势;钢纤维的掺入,粉煤灰轻骨料混凝土裂隙明显减少,同时7d抗折强度满足开放交通要求。研究成果为实践工程提供一定理论基础。
[Abstract]:In order to study the early deformation and crack resistance of steel fiber lightweight aggregate concrete, the volume shrinkage deformation and crack resistance of steel fiber fly ash lightweight aggregate concrete with different contents were tested in laboratory. The experimental results show that adding steel fiber into fly ash lightweight aggregate concrete can effectively inhibit the shrinkage of concrete, and with the increase of steel fiber content, the shrinkage reduction effect becomes more and more remarkable. The compressive strength and splitting tensile strength of fly ash lightweight aggregate concrete are improved to a certain extent, and with the increase of steel fiber content, the crack of fly ash lightweight aggregate concrete decreases obviously with the addition of steel fiber. At the same time, the 7d flexural strength meets the requirements of open traffic. The research results provide a theoretical basis for practical engineering.
【作者单位】： 山西交通职业技术学院;
【分类号】：TU528

【相似文献】

相关期刊论文 前10条

1 周良,李思和;钢纤维生产[J];金属制品;1988年02期

2 翟才旺,高广淳,周雪梅,赵宇;钢纤维喷混凝土加固技术及应用[J];红水河;2002年01期

3 苏波,吴建和;钢纤维喷混凝土性能试验和配合比设计[J];现代隧道技术;2002年04期

4 杨萌;黄承逵;刘毅;;钢纤维高强混凝土抗剪性能试验研究[J];大连理工大学学报;2005年06期

5 何培玲;张厚先;杨平;嵇小雷;杨增文;;钢纤维水泥土无侧限抗压强度试验研究[J];南京工程学院学报(自然科学版);2006年02期

6 冯雨松;;关于钢纤维聚合物水泥混凝土的分析[J];施工技术;2006年S2期

7 谭萍;马芹永;崔磊;;钢纤维混凝土小型空心砌块抗压性能试验与分析[J];新型建筑材料;2008年12期

8 郝永胜;;钢纤维在预制构件及喷射砼中的应用[J];内蒙古民族大学学报;2009年02期

9 欧阳幼玲;陈迅捷;陆采荣;方t，

本文编号：1551842