无机聚合物珊瑚礁砂混凝土基本力学性能试验研究

发布时间：2018-03-02 03:04

  本文关键词： 无机聚合物 珊瑚礁砂 正交试验 力学性能　出处：《武汉理工大学学报》2016年11期 　论文类型：期刊论文

【摘要】：利用珊瑚礁砂为细骨料,无机聚合物为胶凝材料,试配出无机聚合物珊瑚礁砂混凝土(IPCSC);考虑水胶比、胶凝材料用量、砂率以及温度4项因素,进行正交试验,优选出强度等效于C40且工作性能优良的配比;根据标准方法测试了基本力学性能,各项指标与对照的水泥珊瑚礁砂混凝土(CSC)进行了对比。结果表明:相对于对照组,同强度等级时,IPCSC劈裂抗拉强度提高62%,试样拉压强度比增加,静力弹性模量略有提高。
[Abstract]:Using coral reef sand as fine aggregate and inorganic polymer as cementitious material, inorganic polymer coral reef sand concrete was prepared. The orthogonal test was carried out considering four factors: water / binder ratio, amount of cementitious material, sand ratio and temperature. The ratio of strength equivalent to C40 and excellent working performance was selected, and the basic mechanical properties were tested according to the standard method, and the indexes were compared with the control CSCs. The results showed that: compared with the control group, At the same strength grade, the splitting tensile strength of IPCSC increases by 62%, the tensile strength ratio increases, and the static modulus of elasticity increases slightly.
【作者单位】： 武汉理工大学设计研究院;武汉理工大学土木工程与建筑学院;
【基金】：国家科技支撑计划(2014BAB15B01)
【分类号】：TU528

【相似文献】

中国期刊全文数据库 前4条

1 ;新的无机聚合物氯化磷腈首次投产[J];化工新型材料科技资料;1979年10期

2 吴永根;付亚伟;蔡良才;刘洋;王硕太;徐波;;无机聚合物快速修补混凝土研究[J];混凝土;2008年09期

3 梁磊;李晓;牛晚扬;孟瑞晋;;双氧水发泡体系对无机聚合物发泡混凝土硬化性能的影响研究[J];混凝土;2014年01期

4 ;[J];;年期

中国硕士学位论文全文数据库 前2条

1 游纯子;无机聚合物混凝土温度-应力试验研究[D];武汉理工大学;2014年

2 刘骅;无机聚合物混凝土耐久性能试验研究[D];武汉理工大学;2011年

，

本文编号：1554725