聚乙烯醇缩戊二醛对高炉渣棉保温板吸湿率的影响研究

发布时间：2018-10-22 10:40

【摘要】：以实验室自制高炉渣棉纤维为基材,分别采用聚乙烯醇缩戊二醛(PVA-GA)和酚醛树脂为粘结剂制备高炉渣棉纤维板,对两种粘结剂制备的保温板吸湿率和导热系数的考察与对比研究,然后对新型粘结剂进行改性试验,探究其对高炉渣棉保温制品防水性能的影响。结果表明:聚乙烯醇缩戊二醛作粘结剂的高炉渣棉保温板吸湿率为1.14%,有机硅憎水剂改性后的粘结剂制得保温板吸湿率达0.19%,导热系数达到0.020 6 W/(m·K)表现良好。
[Abstract]:The cotton fiber board of blast furnace slag was prepared by using polyvinyl glutaraldehyde (PVA-GA) and phenolic resin as binder. The moisture absorption and thermal conductivity of the two kinds of binders were investigated and compared. The effect of the new binder on the waterproof property of blast furnace slag cotton insulation product was studied. The results show that the moisture absorption rate of the thermal insulation board with polyvinyl alcohol glutaraldehyde as binder is 1.14, the moisture absorption rate of heat preservation board is 0.19 and the thermal conductivity is 0.020 W / (m K) after modification of silicone hydrophobic agent.
【作者单位】： 华北理工大学冶金与能源学院;
【基金】：国家科技支撑计划项目(2012BAE09B02、2012BAE09B03) 国家自然科学基金项目(51274270)
【分类号】：TU551

【相似文献】

相关期刊论文 前7条

1 江大志,唐羽章;环氧-酚醛树脂的湿效应实验研究[J];宇航材料工艺;1992年05期

2 李静;;纤维增强树脂基复合材料的吸湿性和湿变形[J];航天返回与遥感;2010年02期

3 王志平;梁吉勇;张国尚;;GFRP层压板挖补修理后的吸湿行为[J];宇航材料工艺;2014年02期

4 陈莲,赵思孟;稻谷增湿通风调质过程中吸湿率的研究[J];淮海工学院学报(自然科学版);2001年01期

5 孟爽芬,王伟亢,吴维冈,潘金玉;M-84可溶型芯混合料的研究[J];航天工艺;1985年02期

6 张欢;蔡梦军;王程远;吴秋芳;;粘结剂种类和用量对粉煤灰纤维板性能的影响[J];非金属矿;2013年03期

7 ;[J];;年期

相关硕士学位论文 前9条

1 李绍权;氨基酸可释放纤维材料的机理及其表征研究[D];大连工业大学;2011年

2 王国卫;改性煅白的制备及防吸湿研究[D];太原理工大学;2015年

3 何文佳;UH_L/EP复合材料吸湿行为及吸湿应力的有限元分析[D];华南理工大学;2011年

4 梁晓波;原位分散聚合制备防吸湿煅白及其机理研究[D];太原理工大学;2015年

5 龙国峰;吸湿干爽性能纤维的研制[D];苏州大学;2006年

6 孙丽;纤维增强环氧树脂基复合材料吸湿行为的有限元研究[D];天津大学;2007年

7 丁利;熔融复合LDPE/PVA吸湿功能材料的制备[D];浙江大学;2008年

8 王凤仙;以聚乙烯醇为基材的吸湿薄膜研究[D];上海海洋大学;2013年

9 杨荣郭;夏热冬冷地区调湿型涂料的研制[D];湖南工业大学;2013年

，

本文编号：2286926