灰铸铁摆线液压马达壳体铸造工艺优化

发布时间：2018-01-07 19:38

  本文关键词：灰铸铁摆线液压马达壳体铸造工艺优化　出处：《热加工工艺》2017年09期 　论文类型：期刊论文

  更多相关文章： 摆线液压马达壳体 灰铸铁 数值模拟 工艺优化

【摘要】：运用ProCAST软件对灰铸铁BMR型摆线液压马达壳体的铸造工艺进行数值模拟。通过对充型过程和凝固过程的温度场模拟结果分析,预测了壳体铸造缺陷的位置,并对原铸造工艺方案进行了改进。对改进后的方案进行模拟分析和实际验证。结果表明,增加冒口可弥补灰铸铁凝固时自补缩和后补缩不足的差额,且增加冷铁能够有效地加快热节处金属液凝固速度,从而消除了壳体内的缩孔缺陷。
[Abstract]:Using the technology of gray cast iron BMR type cycloid hydraulic motor shell casting ProCAST software. Through the numerical simulation of filling process and solidification temperature field analysis of simulation results, the prediction of shell casting defects, and the original casting process was improved. Simulation analysis and practical verification of the improved scheme. The results show that the increase of the riser can compensate for the gray cast iron during solidification of self feeding and complement the difference shrinkage is insufficient, and the increase of cold iron can effectively accelerate the hot spot in the liquid metal solidification rate, thus eliminating the shrinkage defects in the shell.

【作者单位】： 安徽理工大学机械工程学院;江苏鹏飞集团股份有限公司;
【基金】：国家自然科学基金项目(51205003)
【分类号】：TG251;TH137.51
【正文快照】： BMR系列液压马达是一种内啮合摆线齿轮式液压马达,具有转速范围宽、低速大扭矩、使用可靠、力矩对重量比值大等特点[1]。液压马达正常运转时,其壳体需要有较强的耐冲击性和较高的扭矩承载能力。因此,在壳体铸造过程中不允许有气孔、砂眼、裂纹、缩孔等缺陷。在铸造工艺方案优

【相似文献】

相关期刊论文 前9条

1 董晓强,张树生;液压马达壳体失效分析及修复对策[J];沈阳工业大学学报;1997年02期

2 陈尚友;林远平;陈守安;王进戈;;抛光机上使用液压马达系统和变频器的节能研究[J];河南科技;2013年23期

3 李建设;;液压马达T1—303超高回转精度的控制[J];机床与液压;1993年01期

4 林益平;液压马达导轨内曲面加工用靠模凸轮廓线的计算[J];机械制造;1999年07期

5 熊仕涛;挖掘机液压马达汽缸套失效分析[J];金属热处理;2001年07期

6 刘萍;张东速;;煤气层管道切割装置的研究设计[J];液压与气动;2011年07期

7 ;用于加工推土机各种液压马达壳体的数控组合机床[J];组合机床译丛;1973年S1期

8 张永杰,严喜章,陈成焕;加工液压马达壳体及五星轮的转塔式组合机床[J];组合机床通讯;1979年07期

9 ;[J];;年期

，

本文编号：1393980