有机纤维与聚合物对水泥混凝土层间黏结性能影响研究

发布时间：2018-01-30 04:50

本文关键词： 水泥混凝土层间黏结强度有机纤维聚合物界面剂　出处：《混凝土》2015年01期 　论文类型：期刊论文

【摘要】：水泥混凝土中掺加有机纤维或聚合物能够提高其层间黏结性能。通过层间抗剪强度试验和层间抗拉强度试验方法研究了掺加有机纤维与聚合物对提高水泥混凝土层间黏结强度的效果。对比研究在不同聚合物改性水泥净浆作为界面剂的条件下,水泥混凝土抗拉黏结性能受影响的情况,并对界面剂的配合比;并通过劈裂抗拉黏结性能试验,研究了影响界面黏结性能的浇筑方式和界面黏结剂配合。结果表明:将有机纤维与聚合物掺入水泥混凝土中能够显著提高层间黏结强度,其中丁苯DB-1乳液改性水泥净浆效果最优,尤其当改性水泥净浆作为界面剂的掺量配合比为水泥∶DB-1乳液=3∶2时,新老混凝土可得到较好的层间黏结性能。
[Abstract]:The interlaminar adhesion of cement concrete can be improved by adding organic fiber or polymer to cement concrete. The effect of organic fiber and polymer on the improvement of cement concrete is studied by means of interlaminar shear strength test and interlaminar tensile strength test. The effect of interlaminar bonding strength. A comparative study was carried out under the conditions of different polymer modified cement paste as interfacial agent. Cement concrete tensile bond ability is affected, and the proportion of interfacial agent; The tensile bond properties were tested. The interlayer bonding strength can be improved by mixing organic fiber and polymer into cement concrete. Butadiene DB-1 emulsion modified cement paste is the best, especially when the mixture ratio of modified cement paste as interfacial agent is cement: DB-1 emulsion 3: 2. The new and old concrete can obtain better interlaminar bonding performance.
【作者单位】：中国地质大学(武汉)工程学院土木工程系;
【基金】：国家自然科学基金(51308518)
【分类号】：U414;U416.216
【正文快照】： 0引言从水泥混凝土的使用现状来看,很多早期水泥混凝土路面已接近或者超过计划年限,交通量的发展导致水泥路面所承受的载荷持续增长,路面破坏严重,大大的降低了公路的运输功能和车辆的行驶安全[1]。许多道路面临着艰巨的大修改建任务,其中水泥混凝土罩面层的加铺成为路面大修

【参考文献】