不同纤维掺量下SMA-13路用性能横向对比研究

发布时间：2018-04-25 09:07

  本文选题：道路工程 + SMA-　； 参考：《公路》2017年03期

【摘要】：在原材料和配合比设计基础上,进行SMA-13沥青混合料的马歇尔试验、高温车辙试验、低温弯曲试验、水稳定性试验及析漏飞散试验,对木质纤维和3种矿质纤维在不同掺量下SMA-13路用性能进行了横向对比。研究结果表明:掺加木质纤维的SMA-13沥青混合料吸油效果和路用性能最好;针对文中选用的矿质2号、矿质3号和矿质4号3种矿质纤维,3号矿质纤维的吸油性和路用性能较好。
[Abstract]:On the basis of raw material and mix ratio design, Marshall test, high temperature rutting test, low temperature bending test, water stability test and leakage and dispersion test of SMA-13 asphalt mixture are carried out. The road performance of wood fiber and three mineral fibers under different contents of SMA-13 were compared horizontally. The results show that the oil absorption effect and road performance of SMA-13 asphalt mixture with wood fiber are the best, and the oil absorption and road performance of No. 3 mineral fiber are better than that of mineral fiber No. 3 and mineral fiber No. 4, which are selected in this paper.
【作者单位】： 沈阳建筑大学交通工程学院;
【基金】：国家自然科学基金项目,项目编号51178278
【分类号】：U414

【相似文献】

相关期刊论文 前10条

1 刘俊龙;杨颖;郑贝利;;SMA-13混合料配合比设计[J];公路;2009年06期

2 陈晋华;;SMA-13沥青混合料配合比设计[J];黑龙江工程学院学报(自然科学版);2011年02期

3 欧阳文杰;;沥青玛蹄脂碎石混合料(改性沥青)SMA-13配合比设计实例探析[J];城市建筑;2013年12期

4 李芸;李小洪;;橡胶沥青SMA-13施工工艺研究[J];西南公路;2014年01期

5 黄明池;;改性沥青玛蹄脂碎石混合料上面层SMA-13质量控制[J];四川建材;2012年03期

6 林少扬;SMA-13沥青混合料配合比设计总结[J];城市道桥与防洪;2004年02期

7 胡欣;;改性沥青混合料SMA-13上面层的压实施工[J];建材技术与应用;2008年11期

8 周永军;;四川乐峨公路改造中SMA-13配合比设计及施工[J];公路交通技术;2009年05期

9 吴善周,钟梦武,吴超凡,黄开宇,谢祥根;衡枣高速公路SMA-13的设计与施工[J];湖南交通科技;2003年04期

10 韩勇强;张萍;;轮胎压路机在SMA-13沥青混合料路面施工中的应用[J];中国市政工程;2011年02期

相关硕士学位论文 前2条

1 高建;矿物纤维在SMA-13沥青路面中的应用研究[D];重庆交通大学;2013年

2 童晓斌;SMA-13上面层施工技术应用与控制研究[D];长安大学;2012年

，

本文编号：1800671